Effects of massive laser shock peening (LSP) treatment as a function of coverage layer on surface residual stress, microstructure, and corrosion fatigue (CF) resistance of Fe-Cr alloy were studied by X-ray diffraction technique, scanning electron microscope observations, and corrosion fatigue crack growth (CFCG) testing. Special attention was paid to the details of compressive residual stress and fracture morphology, and the influence mechanism of coverage layer on CF behaviour was also determined. Results indicated that LSP generated deeper compressive residual stress and effectively decreased the CFCG rate, and increased coverage layers further improved the corrosion fatigue life of notched specimens.

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effects of Laser Shock Peening with Different Coverage Layers on Fatigue Behaviour and Fractural Morphology of Fe–Cr Alloy in NaCl Solution

  • 章节

  • 发表日期：

    2025年

查看全文
  • Kaiyu Luo,
  • Changyu Wang,
  • Jinzhong Lu

摘要

Effects of massive laser shock peening (LSP) treatment as a function of coverage layer on surface residual stress, microstructure, and corrosion fatigue (CF) resistance of Fe-Cr alloy were studied by X-ray diffraction technique, scanning electron microscope observations, and corrosion fatigue crack growth (CFCG) testing. Special attention was paid to the details of compressive residual stress and fracture morphology, and the influence mechanism of coverage layer on CF behaviour was also determined. Results indicated that LSP generated deeper compressive residual stress and effectively decreased the CFCG rate, and increased coverage layers further improved the corrosion fatigue life of notched specimens.