This study investigated the distribution of steel corrosion products in a cracked concrete beam, which was in service under coastal atmospheric conditions for more than 40 years. The thickness of corrosion-product-filled paste (CP) and the thickness of corrosion layer (CL) were measured. The migration behaviour of Fe in the concrete cracks and air voids are investigated. The mechanism of CP formation was revealed. The steel corrosion and corrosion-product-filled paste propagates faster in the tension region than in the compressive region of the beam. In the atmospheric environment, the corrosion products neither fill the cracks or air voids nor do they accumulate on the edge of the cracks or inside the air voids.

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Distribution of Steel Corrosion Products in a Cracked Concrete Beam Exposed to Coastal Atmosphere

  • 章节

  • 出版模式：

    开放获取

  • 发表日期：

    2025年

查看全文
  • Jianfeng Dong,
  • Xuepeng Lin,
  • Xueyuan Liu,
  • Jianzong Guo,
  • Yuxi Zhao

摘要

This study investigated the distribution of steel corrosion products in a cracked concrete beam, which was in service under coastal atmospheric conditions for more than 40 years. The thickness of corrosion-product-filled paste (CP) and the thickness of corrosion layer (CL) were measured. The migration behaviour of Fe in the concrete cracks and air voids are investigated. The mechanism of CP formation was revealed. The steel corrosion and corrosion-product-filled paste propagates faster in the tension region than in the compressive region of the beam. In the atmospheric environment, the corrosion products neither fill the cracks or air voids nor do they accumulate on the edge of the cracks or inside the air voids.