摘要
This book mainly describes the fracture behavior of heat-resistant austenitic stainless steel SUS304 under high-temperature creep-fatigue, especially under the conditions that exhibit inner cracking type fracture, from the onset to the final failure. Typical damage of austenitic stainless steel SUS304 caused by creep-fatigue is grain boundary cavities, small intergranular cracks, and large cracks.