Superconducting Properties of 2G HTS Wires Irradiated by Bi Ions with Energy 670 MeV
摘要
Abstract
The investigation results of magnetization, dynamic magnetic susceptibility and microstructure of samples of second generation high-temperature superconducting wires irradiated by Bi ions at room temperature with energy of 670 MeV and fluences of 1011 and 1012 cm–2 are presented. The dependences of the superconducting transition temperature and critical current density on the fluence have been determined. For the sample irradiated to fluence 1011 cm–2, an increase in the critical current density is observed compared to the control nonirradiated sample. The microstructure analysis of irradiated samples demonstrates the presence of amorphous tracks, which can act as effective pinning centers.