<p>Poly(lactide-co-glycolide) (PLGA) is widely used in a variety of long-acting injectables. However, its biodegradable nature creates potential chemical stability challenges during melt extrusion, where PLGA is exposed to elevated temperature (100–140&#xa0;°C) for several minutes. This study evaluated the thermal stability of three PLGA grades (Resomer® 502, 502H, and 505) with varying molecular weights and chain-ends using a differential scanning calorimeter and twin-screw extruder. DSC results revealed that both residual water content and chain-end groups significantly accelerate PLGA degradation. At 0.2% water content, all samples maintained good stability (less than 15% reduction in molecular weight). However, at 0.4% water content, Resomer 502H, which has acid end groups, experienced significant degradation (45% reduction in molecular weight) after 30&#xa0;min at 140&#xa0;°C due to catalyzed hydrolysis. The extruded samples remained stable across tested barrel temperatures (100&#xa0;°C and 140&#xa0;°C) and screw speeds (125 and 250&#xa0;rpm). Further investigations of PLGA with 0.2% water content demonstrates that the hydrolysis rates of Resomer® 502 and 505 were comparable, indicating that molecular weight does not influence hydrolysis rate. In contrast, Resomer® 502H exhibited a higher hydrolysis rate and a slightly higher activation energy, suggesting a greater temperature dependency. Additionally, when subjected to 200&#xa0;°C for one hour with less than 0.03% water content, Resomer® 505 showed a less than 7% reduction in molecular weight, indicating minimal thermal degradation. Conversely, Resomer® 502 and 502H experienced an increase in molecular weight, which was likely attributed to recombination reactions, particularly in Resomer® 502H, which has higher tin content (170&#xa0;ppm).</p> Graphical Abstract <p></p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Investigation of the Thermal Stability and Hydrolytic Degradation Kinetics of Poly(Lactide-co-Glycolide) Melts

  • 期刊论文

  • 发表日期：

    2025年1月8日

查看全文
  • Beibei Chen,
  • Mark A. Costello,
  • Louise Kuehster,
  • Nathaniel A. Lynd,
  • Bin Qin,
  • Yan Wang,
  • Feng Zhang

摘要

Poly(lactide-co-glycolide) (PLGA) is widely used in a variety of long-acting injectables. However, its biodegradable nature creates potential chemical stability challenges during melt extrusion, where PLGA is exposed to elevated temperature (100–140 °C) for several minutes. This study evaluated the thermal stability of three PLGA grades (Resomer® 502, 502H, and 505) with varying molecular weights and chain-ends using a differential scanning calorimeter and twin-screw extruder. DSC results revealed that both residual water content and chain-end groups significantly accelerate PLGA degradation. At 0.2% water content, all samples maintained good stability (less than 15% reduction in molecular weight). However, at 0.4% water content, Resomer 502H, which has acid end groups, experienced significant degradation (45% reduction in molecular weight) after 30 min at 140 °C due to catalyzed hydrolysis. The extruded samples remained stable across tested barrel temperatures (100 °C and 140 °C) and screw speeds (125 and 250 rpm). Further investigations of PLGA with 0.2% water content demonstrates that the hydrolysis rates of Resomer® 502 and 505 were comparable, indicating that molecular weight does not influence hydrolysis rate. In contrast, Resomer® 502H exhibited a higher hydrolysis rate and a slightly higher activation energy, suggesting a greater temperature dependency. Additionally, when subjected to 200 °C for one hour with less than 0.03% water content, Resomer® 505 showed a less than 7% reduction in molecular weight, indicating minimal thermal degradation. Conversely, Resomer® 502 and 502H experienced an increase in molecular weight, which was likely attributed to recombination reactions, particularly in Resomer® 502H, which has higher tin content (170 ppm).

Graphical Abstract