Mechanical and chemical characterization of biochar-reinforced polystyrene composites

This study investigates the chemical interactions and mechanical characteristics of composites made of polystyrene reinforced with biochar. Polystyrene-based resin (PBR) was combined with plantain peel-derived biochar in different weight ratios (10%, 20%, 30%, and 40%). The Brinell hardness test, Fourier transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS) were used to evaluate the properties of the composites. The results of the hardness test showed a non-monotonic pattern, with hardness first decreasing at low biochar loadings (10% and 20%), then significantly increasing at 30% biochar. At 40% biochar, the hardness then somewhat dropped, indicating that around 30% filler is the optimal biochar level for hardness. As the biochar loading increased, FTIR measurement showed that hydroxyl groups (-OH) were introduced and that the intensity of carbonyl groups (C = O) increased. According to SEM analysis, a uniform surface was found at lower biochar loadings, but at larger biochar contents, the surface became irregular and rough. In addition to providing insights into the chemical interactions at the interface between the biochar and the polymer matrix, these findings demonstrate the possibility of incorporating biochar to alter the mechanical properties of PBR.