Enamel changes of bleached teeth following application of an experimental combination of chitosan-bioactive glass

Considering the extensive use of bleaching agents and the occurrence of side effects such as enamel demineralization, this study aimed to assess the enamel changes of bleached teeth following the experimental application of chitosan-bioactive glass (CH-BG).

In this in vitro study, CH-BG (containing 66% BG) was synthesized and characterized by Fourier-transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD). Thirty sound human premolars were bleached with 40% hydrogen peroxide, and the weight% of calcium and phosphorus elements of the buccal enamel surface was quantified before and after bleaching by scanning electron microscopy/ energy-dispersive X-ray spectroscopy (SEM, EDX). Depending on the surface treatment of the enamel surface, the specimens were divided into three groups (n = 10): control (no treatment), MI Paste (MI), and CH-BG. Then the specimens were stored in artificial saliva for 14 days. The SEM/EDX analyses were performed again on the enamel surface. Data were analyzed by one-way ANOVA and Tukey’s test and a p-value of < 0.05 was considered statistically significant.

In all groups, the weight% of calcium and phosphorus elements of enamel decreased after bleaching; this reduction was significant for phosphorus (p < 0.05) and insignificant for calcium (p > 0.05). After 14 days of remineralization, the weight% of both calcium and phosphorus elements was significantly higher compared to their bleached counterparts in both MI and CH-BG groups (p < 0.05). Following the remineralization process, the difference between MI and CH-BG groups was not significant (p > 0.05) but both had a significant difference with the control group in this regard (p < 0.05).

The synthesized CH-BG compound showed an efficacy comparable to that of MI Paste for enamel remineralization of bleached teeth.