<p><b>Abstract</b>—This research studied the effect of centrifugal casting on the mechanical properties of deformable semi-finished products made of aluminum alloys of the Al–Zn–Mg–Cu and Al–Mg systems for space technology products. The study was carried out on sheets with a thickness of 3 mm and a rolling ring with a thickness of 10 mm. The samples were obtained from annular cast blanks measuring 350/240 mm (outer/inner diameter) cast by centrifugal casting. Hardness measurements were carried out along the width of the cast ring. The measurement results showed that the hardness practically did not change over the entire width, except for a zone at a distance of 5 to 7 mm from the inner edge of the ring. In this zone, the hardness decreases sharply. It has been determined that deformed semi-finished products obtained from blanks cast by centrifugal casting have minimal anisotropy of strength properties. The properties of the rolling ring of the Al–Mg alloy system exceed the properties of similar products manufactured using standard technologies. The proposed technology for manufacturing solid-rolled rings from blanks obtained by centrifugal casting will not only increase the reliability of products with a significant reduction in labor intensity, but also reduce their weight by increasing their mechanical characteristics.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Centrifugal Casting of Aluminum Alloys as a Method for Obtaining Semi-Finished Products with an Increased Set of Properties for Space Technology Products

  • 期刊论文

  • 发表日期：

    2025年9月24日

查看全文
  • P. Yu. Predko,
  • D. I. Maiorov,
  • N. D. Shanin,
  • A. A. Alpatov,
  • S. G. Bochvar

摘要

Abstract—This research studied the effect of centrifugal casting on the mechanical properties of deformable semi-finished products made of aluminum alloys of the Al–Zn–Mg–Cu and Al–Mg systems for space technology products. The study was carried out on sheets with a thickness of 3 mm and a rolling ring with a thickness of 10 mm. The samples were obtained from annular cast blanks measuring 350/240 mm (outer/inner diameter) cast by centrifugal casting. Hardness measurements were carried out along the width of the cast ring. The measurement results showed that the hardness practically did not change over the entire width, except for a zone at a distance of 5 to 7 mm from the inner edge of the ring. In this zone, the hardness decreases sharply. It has been determined that deformed semi-finished products obtained from blanks cast by centrifugal casting have minimal anisotropy of strength properties. The properties of the rolling ring of the Al–Mg alloy system exceed the properties of similar products manufactured using standard technologies. The proposed technology for manufacturing solid-rolled rings from blanks obtained by centrifugal casting will not only increase the reliability of products with a significant reduction in labor intensity, but also reduce their weight by increasing their mechanical characteristics.