Abstract <p>Castings based on a ceramic suspension containing 80 wt % VK94-1 powder were produced using the gel casting method. A gel-forming agent system based on acrylamide (the main monomer) and methylene bisacrylamide (the crosslinking monomer) was used. The sintered ceramic is characterized by a fine crystalline structure with a grain size of 2–8 μm and a uniform distribution of glass phase layers, with a relative density of up to 93% and an ultimate bending strength of up to 332 MPa.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Gel Casting of Parts from VK94-1 Ceramic

  • 期刊论文

  • 发表日期：

    2025年8月2日

查看全文
  • I. E. Golubeva,
  • A. I. Sitnikov,
  • K. A. Solntsev

摘要

Abstract

Castings based on a ceramic suspension containing 80 wt % VK94-1 powder were produced using the gel casting method. A gel-forming agent system based on acrylamide (the main monomer) and methylene bisacrylamide (the crosslinking monomer) was used. The sintered ceramic is characterized by a fine crystalline structure with a grain size of 2–8 μm and a uniform distribution of glass phase layers, with a relative density of up to 93% and an ultimate bending strength of up to 332 MPa.