Abstract <p>The effects of pH and temperature during synthesis on the pore structure and morphology of porous silica were investigated using inexpensive polyethylene glycol as a template. At a synthesis temperature of 20°C, the porous silica obtained at pH 4.0–6.0 mainly exhibited micropores, while those obtained at pH 7.0 and 8.0 developed both micropores and mesopores. At pH 7, increasing the synthesis temperature resulted in the formation of more mesopores and the production of smaller spherical porous silica particles. At pH 7 and a temperature of 60°C, spherical porous silica with a specific surface area of 654.6 m<sup>2</sup>/g and an average particle size of 0.8 µm was obtained.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Effect of Synthesis Conditions on the Morphology and Pore Structure of Spherical Porous Silica Synthesized Using Polyethylene Glycol as a Template

  • 期刊论文

  • 发表日期：

    2025年2月1日

查看全文
  • Kazuya Tanji,
  • Atsuki Kimura,
  • Teruhisa Hongo

摘要

Abstract

The effects of pH and temperature during synthesis on the pore structure and morphology of porous silica were investigated using inexpensive polyethylene glycol as a template. At a synthesis temperature of 20°C, the porous silica obtained at pH 4.0–6.0 mainly exhibited micropores, while those obtained at pH 7.0 and 8.0 developed both micropores and mesopores. At pH 7, increasing the synthesis temperature resulted in the formation of more mesopores and the production of smaller spherical porous silica particles. At pH 7 and a temperature of 60°C, spherical porous silica with a specific surface area of 654.6 m2/g and an average particle size of 0.8 µm was obtained.