Abstract <p>The time dependences of the contact angles and the wetted surface spot diameters have been measured during the interaction between Co–Cu melts with copper contents of 20, 40, and 60 at % and graphite at temperatures of 1390, 1440, 1490, 1540, and 1590°C. Under these conditions, graphite is not wetted by the Co–Cu melts: the final contact angles for Co80–Cu20, Co60–Cu40, and Co40–Cu60 are 95, 110, and 100°, respectively. Therewith, the final diameters of the wetted surface spots somewhat increase. The metallographic analysis of the microstructure of the Co–Cu–C composite materials obtained by the contact alloying of Co–Cu melts with carbon has shown that the morphology of the structural components and the phase composition of the samples depend on the copper content. Composite materials (Co–27%C–10%Cu) + (Co–32%C–62%Cu) + C and (Co–19%C–15%Cu) + (Co–25%C–72%Cu) + C obtained by the interaction of the Co–Cu melts containing 20 and 40 at % copper with graphite have a macrohomogeneous structure.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Kinetics of the Interaction of Co–Cu Melts with Graphite and Microstructure of Formed Metal–Carbon Composites

  • 期刊论文

  • 发表日期：

    2025年2月1日

查看全文
  • O. A. Chikova,
  • I. G. Shirinkina,
  • V. S. Tsepelev,
  • N. I. Sinitsin,
  • V. V. Vyukhin

摘要

Abstract

The time dependences of the contact angles and the wetted surface spot diameters have been measured during the interaction between Co–Cu melts with copper contents of 20, 40, and 60 at % and graphite at temperatures of 1390, 1440, 1490, 1540, and 1590°C. Under these conditions, graphite is not wetted by the Co–Cu melts: the final contact angles for Co80–Cu20, Co60–Cu40, and Co40–Cu60 are 95, 110, and 100°, respectively. Therewith, the final diameters of the wetted surface spots somewhat increase. The metallographic analysis of the microstructure of the Co–Cu–C composite materials obtained by the contact alloying of Co–Cu melts with carbon has shown that the morphology of the structural components and the phase composition of the samples depend on the copper content. Composite materials (Co–27%C–10%Cu) + (Co–32%C–62%Cu) + C and (Co–19%C–15%Cu) + (Co–25%C–72%Cu) + C obtained by the interaction of the Co–Cu melts containing 20 and 40 at % copper with graphite have a macrohomogeneous structure.