Mechanical Properties and Fracture of Ultrafine-Grained Near β Titanium Alloy under Three-Point Bending

期刊论文
发表日期：

2024年12月8日

查看全文

E. V. Naydenkin,
I. P. Mishin,
I. V. Ratochka,
B. B. Straumal,
O. V. Zabudchenko,
O. N. Lykova,
A. I. Manisheva

摘要

Abstract

Comparative studies are conducted on the structure and mechanical properties of the ultrafine-grained Ti-5Al-5V-5Mo-1Cr-1Fe alloy obtained by abc pressing and radial shear rolling with subsequent aging. It is shown that the ultrafine-grained structure formed by these methods provides increased strength properties under both tension and three-point bending compared to the initial coarse-grained state. At the same time, the alloy obtained by abc pressing demonstrates a higher fracture resistance during three-point bending compared to the alloy obtained by radial shear rolling + aging due to its enhanced ductility. This also determines the ductile fracture pattern of the ultrafine-grained alloy obtained by abc pressing during three-point bending in contrast to ductile-brittle fracture of the alloy obtained by radial shear rolling + aging.