<p>Heat-resistant steels with high chromium additions (≥5 weight percent) are critical for many high temperature energy and manufacturing applications, including heat exchangers, pistons for engines, and dies for metal working and casting. However, while high chromium additions increase oxidation resistance at elevated temperatures, they also compromise thermal conductivity, resulting in a metallurgical trade-off between these two important properties. Here we show that a microstructure with both higher thermal conductivity and improved oxidation resistance at elevated temperatures is achieved in a unique steel with only 1 weight percent chromium, thereby overcoming the long-standing metallurgical trade-off. This is accomplished through a tailored thermal treatment that produces a tempered martensitic matrix with low solute content and a fine dispersion of copper precipitates and molybdenum enriched carbides. A further discovery is that the resultant thermally grown oxide includes an iron-copper-manganese-enriched outer layer that provides high-temperature oxidation protection equivalent to heat-resistant steels with five times the chromium content and 25% lower thermal conductivity.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Overcoming the thermal conductivity versus oxidation resistance barrier in high-temperature steels

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年11月20日

查看全文
  • Dean Pierce,
  • Rishi Pillai,
  • Hsin Wang,
  • Jon Poplawsky,
  • James Haynes,
  • Katherine Sebeck,
  • Michael Tess,
  • Eric Gingrich,
  • Govindarajan Muralidharan

摘要

Heat-resistant steels with high chromium additions (≥5 weight percent) are critical for many high temperature energy and manufacturing applications, including heat exchangers, pistons for engines, and dies for metal working and casting. However, while high chromium additions increase oxidation resistance at elevated temperatures, they also compromise thermal conductivity, resulting in a metallurgical trade-off between these two important properties. Here we show that a microstructure with both higher thermal conductivity and improved oxidation resistance at elevated temperatures is achieved in a unique steel with only 1 weight percent chromium, thereby overcoming the long-standing metallurgical trade-off. This is accomplished through a tailored thermal treatment that produces a tempered martensitic matrix with low solute content and a fine dispersion of copper precipitates and molybdenum enriched carbides. A further discovery is that the resultant thermally grown oxide includes an iron-copper-manganese-enriched outer layer that provides high-temperature oxidation protection equivalent to heat-resistant steels with five times the chromium content and 25% lower thermal conductivity.