<p>Stacking orders and topological defects substantially influence the physical properties of 2D van der Waals (vdW) materials. However, the inherent features of 2D materials challenge the effectiveness of single characterization techniques in identifying stacking sequences, necessitating correlative approaches. Using bilayer MoS<sub>2</sub> as a benchmark, we differentiate its polytypism and specific dislocations through transmission electron microscopy (TEM) and Raman spectroscopy. Perfect and partial dislocations were revealed in TEM, which are closely linked to the stacking sequences, thus indirectly indicating the 2H and 3R polytypes. Quantitative analysis of reciprocal lattice from 3D electron diffraction and low-frequency Raman spectroscopy further validated these polytypes owing to their reliance on crystal symmetry. Surprisingly, we unexpectedly resolved both polytypes despite starting with 2H bulk crystal, pointing to a possible phase transition during mechanical exfoliation. The correlative TEM-Raman approach can be extended to other 2D materials, paving the way for property alteration via stacking and defect engineering.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Identification of polytypism and their dislocations in bilayer MoS2 using correlative transmission electron microscopy and Raman spectroscopy

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月5日

查看全文
  • Xin Zhou,
  • Tobias Dierke,
  • Mingjian Wu,
  • Shengbo You,
  • Klaus Götz,
  • Tobias Unruh,
  • Philipp Pelz,
  • Johannes Will,
  • Janina Maultzsch,
  • Erdmann Spiecker

摘要

Stacking orders and topological defects substantially influence the physical properties of 2D van der Waals (vdW) materials. However, the inherent features of 2D materials challenge the effectiveness of single characterization techniques in identifying stacking sequences, necessitating correlative approaches. Using bilayer MoS2 as a benchmark, we differentiate its polytypism and specific dislocations through transmission electron microscopy (TEM) and Raman spectroscopy. Perfect and partial dislocations were revealed in TEM, which are closely linked to the stacking sequences, thus indirectly indicating the 2H and 3R polytypes. Quantitative analysis of reciprocal lattice from 3D electron diffraction and low-frequency Raman spectroscopy further validated these polytypes owing to their reliance on crystal symmetry. Surprisingly, we unexpectedly resolved both polytypes despite starting with 2H bulk crystal, pointing to a possible phase transition during mechanical exfoliation. The correlative TEM-Raman approach can be extended to other 2D materials, paving the way for property alteration via stacking and defect engineering.