<p>The long-term durability of natural fibre-reinforced bio-composites under hygrothermal environments remains a major barrier to their deployment in building and construction. This study provides a methodical evaluation of the mechanical, viscoelastic, and chemical degradation mechanisms of bio-epoxy composites reinforced with alkali-treated sunn hemp fibres (SHFs) under accelerated hygrothermal ageing (60&#xa0;°C, 98% RH, up to 3,000&#xa0;h). Fibre modification was performed using sodium hydroxide (NaOH) concentrations of 6%, 8%, and 10% for 2&#xa0;h to investigate the influence of treatment severity on durability. Moisture uptake followed Fickian diffusion behaviour, with the 8% NaOH condition exhibiting the lowest equilibrium moisture content (13.5%) due to controlled removal of amorphous constituents and improved fibre–matrix compatibility. While tensile and interlaminar shear strength (ILSS) decreased with exposure time, a treatment-dependent trade-off was identified: 8% NaOH maximised initial mechanical performance, whereas 10% NaOH provided comparatively superior long-term strength retention. Dynamic mechanical analysis (DMA) demonstrated sustained viscoelastic stability, with the 8% system retaining a storage modulus of 7 GPa at ~ 25&#xa0;°C (glassy region) and a glass transition temperature of 83&#xa0;°C after prolonged exposure. Fourier-transform infrared (FTIR) analysis revealed moderated carbonyl development in optimally treated systems, linking chemical stability to mechanical retention. These results establish a conceptual framework describing the balance between interfacial strengthening and ageing resistance in SHF-reinforced bio-composites, offering predictive insights for service-life design in low-carbon construction applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Hygrothermal ageing and mechanical degradation behaviour of alkali-treated sunn hemp fibre/bio-epoxy composites

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2026年4月28日

查看全文
  • Babatunde Olatunbosun,
  • Allan Manalo,
  • Thiru Aravinthan,
  • Guangnan Chen,
  • Shanika Kiriella,
  • Libo Yan

摘要

The long-term durability of natural fibre-reinforced bio-composites under hygrothermal environments remains a major barrier to their deployment in building and construction. This study provides a methodical evaluation of the mechanical, viscoelastic, and chemical degradation mechanisms of bio-epoxy composites reinforced with alkali-treated sunn hemp fibres (SHFs) under accelerated hygrothermal ageing (60 °C, 98% RH, up to 3,000 h). Fibre modification was performed using sodium hydroxide (NaOH) concentrations of 6%, 8%, and 10% for 2 h to investigate the influence of treatment severity on durability. Moisture uptake followed Fickian diffusion behaviour, with the 8% NaOH condition exhibiting the lowest equilibrium moisture content (13.5%) due to controlled removal of amorphous constituents and improved fibre–matrix compatibility. While tensile and interlaminar shear strength (ILSS) decreased with exposure time, a treatment-dependent trade-off was identified: 8% NaOH maximised initial mechanical performance, whereas 10% NaOH provided comparatively superior long-term strength retention. Dynamic mechanical analysis (DMA) demonstrated sustained viscoelastic stability, with the 8% system retaining a storage modulus of 7 GPa at ~ 25 °C (glassy region) and a glass transition temperature of 83 °C after prolonged exposure. Fourier-transform infrared (FTIR) analysis revealed moderated carbonyl development in optimally treated systems, linking chemical stability to mechanical retention. These results establish a conceptual framework describing the balance between interfacial strengthening and ageing resistance in SHF-reinforced bio-composites, offering predictive insights for service-life design in low-carbon construction applications.