<p>This study details the hydrothermal synthesis and characterization of SnO<sub>2</sub>/nanocellulose (NC) nanocomposites, highlighting their potential for advanced applications. X-ray diffraction (XRD) analysis confirmed the amorphous nature of the composites, with a broad peak at 25.6° and a rightward shift indicating strong SnO<sub>2</sub>-NC interactions. A sharp peak at 32.26° in the SnO<sub>2</sub>-20 sample signified a rutile structure with single-plane crystallinity. UV-Vis absorption spectra showed a significant blue shift, with bandgap values reaching 5.86&#xa0;eV for SnO<sub>2</sub>-5, compared to 3.6&#xa0;eV for pure SnO<sub>2</sub>, demonstrating enhanced optical properties. Photoluminescence (PL) spectra revealed prominent emissions at 384&#xa0;nm and 486&#xa0;nm, attributed to oxygen vacancies and defect states, which enhance luminescence and support optoelectronic applications. FTIR spectroscopy identified a peak at 3430&#xa0;cm<sup>−1</sup>, confirming abundant hydroxyl groups on cellulose surfaces and high sample purity. Scanning electron microscopy (SEM) images showed uniformly distributed SnO<sub>2</sub> nanoparticles on an amorphous NC matrix, with rod-like features contributing to irregular morphologies that impact defect density and optical behavior. These structural and optical improvements enhance charge transport and reduce carrier recombination, establishing SnO<sub>2</sub>-NC nanocomposites as promising materials for optoelectronic devices, gas sensors, and photocatalysis. The integration of eco-friendly nanocellulose offers a sustainable pathway for developing next-generation technologies with superior performance.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Hydrothermal synthesis of SnO2/cellulose nanocomposites: optical, Structural, and morphological characterization

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年3月21日

查看全文
  • Y. C. Goswami,
  • R. Bisauriya,
  • Ranjana Goswami,
  • A. A. Hlaing,
  • T. T. Moe

摘要

This study details the hydrothermal synthesis and characterization of SnO2/nanocellulose (NC) nanocomposites, highlighting their potential for advanced applications. X-ray diffraction (XRD) analysis confirmed the amorphous nature of the composites, with a broad peak at 25.6° and a rightward shift indicating strong SnO2-NC interactions. A sharp peak at 32.26° in the SnO2-20 sample signified a rutile structure with single-plane crystallinity. UV-Vis absorption spectra showed a significant blue shift, with bandgap values reaching 5.86 eV for SnO2-5, compared to 3.6 eV for pure SnO2, demonstrating enhanced optical properties. Photoluminescence (PL) spectra revealed prominent emissions at 384 nm and 486 nm, attributed to oxygen vacancies and defect states, which enhance luminescence and support optoelectronic applications. FTIR spectroscopy identified a peak at 3430 cm−1, confirming abundant hydroxyl groups on cellulose surfaces and high sample purity. Scanning electron microscopy (SEM) images showed uniformly distributed SnO2 nanoparticles on an amorphous NC matrix, with rod-like features contributing to irregular morphologies that impact defect density and optical behavior. These structural and optical improvements enhance charge transport and reduce carrier recombination, establishing SnO2-NC nanocomposites as promising materials for optoelectronic devices, gas sensors, and photocatalysis. The integration of eco-friendly nanocellulose offers a sustainable pathway for developing next-generation technologies with superior performance.