<p>Rice husk is an agricultural waste from rice milling and nowadays represents an important substitute of silica in synthesis protocols of industrial minerals. Synthesis of monomineralic powders of Analcime by rice husk is here achieved with the conventional hydrothermal method; an improvement in synthesis conditions compared to the past is achieved by lowering rice-husk calcination temperatures, synthesis temperatures, crystallization times and by avoiding aging times. Rice husk is subjected to calcination at the temperature of 550&#xa0;°C and then mixed with NaOH and NaAlO<sub>2</sub>. The experiment is performed at environment pressure and 170 ± 0.1&#xa0;°C for 77&#xa0;h. Analcime is characterized by X-ray diffraction, scanning electron microscopy, infrared and Raman spectroscopy. Cell parameters and the amount of amorphous phase in the synthesis powders is described with quantitative phase analysis using the combined Rietveld and reference intensity ratio methods. The degree of purity of Analcime is calculated in 97,53% at 12&#xa0;h. The results show that rice husk waste represents a good alternative silicon source, and it can be used to produce pure analcime crystals.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Rice husk as raw material in the synthesis of analcime

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年11月3日

查看全文
  • Daniela Novembre,
  • Domingo Gimeno,
  • Lucia Marinangeli,
  • Anna Chiara Tangari,
  • Gianluigi Rosatelli,
  • Michele Ciulla,
  • Pietro di Profio

摘要

Rice husk is an agricultural waste from rice milling and nowadays represents an important substitute of silica in synthesis protocols of industrial minerals. Synthesis of monomineralic powders of Analcime by rice husk is here achieved with the conventional hydrothermal method; an improvement in synthesis conditions compared to the past is achieved by lowering rice-husk calcination temperatures, synthesis temperatures, crystallization times and by avoiding aging times. Rice husk is subjected to calcination at the temperature of 550 °C and then mixed with NaOH and NaAlO2. The experiment is performed at environment pressure and 170 ± 0.1 °C for 77 h. Analcime is characterized by X-ray diffraction, scanning electron microscopy, infrared and Raman spectroscopy. Cell parameters and the amount of amorphous phase in the synthesis powders is described with quantitative phase analysis using the combined Rietveld and reference intensity ratio methods. The degree of purity of Analcime is calculated in 97,53% at 12 h. The results show that rice husk waste represents a good alternative silicon source, and it can be used to produce pure analcime crystals.