<p>Bifunctional MOF-303 (Al) exhibits promising catalytic activity for the Biginelli reaction. However, its intrinsic microporosity may hinder reactant and product diffusion and reducing efficiency. Introducing defects is crucial for enhancing its catalytic performance. In this work, defect-rich MOF-303 was prepared by grinding the hydrothermally synthesized MOF-303 into a fine powder. The resulting material was thoroughly characterized and exhibited excellent catalytic performance in the solvent-free synthesis of diverse dihydropyrimidinones under moderate reaction conditions, achieving yields ranging from 86 to 99%. Moreover, the catalyst was successfully recycled over five cycles with minimal activity loss. The structures of the obtained products were confirmed by IR, <sup>1</sup>H NMR, and melting point analysis. The simple preparation method using commercially inexpensive reagents, high catalytic performance under mild conditions, and recyclability of defect-rich MOF-303 highlight its potential as an efficient and sustainable catalyst for the Biginelli reaction.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Defect-rich MOF-303 as a dual acid–base heterogeneous catalyst for the one-pot Biginelli synthesis of dihydropyrimidinones

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年10月24日

查看全文
  • Nuhaa Shaheed,
  • Ahmad Shaabani

摘要

Bifunctional MOF-303 (Al) exhibits promising catalytic activity for the Biginelli reaction. However, its intrinsic microporosity may hinder reactant and product diffusion and reducing efficiency. Introducing defects is crucial for enhancing its catalytic performance. In this work, defect-rich MOF-303 was prepared by grinding the hydrothermally synthesized MOF-303 into a fine powder. The resulting material was thoroughly characterized and exhibited excellent catalytic performance in the solvent-free synthesis of diverse dihydropyrimidinones under moderate reaction conditions, achieving yields ranging from 86 to 99%. Moreover, the catalyst was successfully recycled over five cycles with minimal activity loss. The structures of the obtained products were confirmed by IR, 1H NMR, and melting point analysis. The simple preparation method using commercially inexpensive reagents, high catalytic performance under mild conditions, and recyclability of defect-rich MOF-303 highlight its potential as an efficient and sustainable catalyst for the Biginelli reaction.