<p>Bacterial infections are among the foremost causes of morbidity and mortality on a global scale. In this study, TiO<sub>2</sub> layers were performed on Ti45Nb alloys by anodic oxidation (AO) process with low voltages. Thus, the aim of this research is to investigate the surface properties, wettability and antimicrobial properties of TiO<sub>2</sub> layers fabricated at low AO voltages on Ti45Nb alloy. The phase structures, morphologies and elemental amounts and distribution of the surfaces were characterized by XRD, Micro-Raman, SEM and EDX. The existence of anatase-TiO<sub>2</sub> was verified on AO layer on Ti45Nb alloy. The wettability of AO layers improved with increasing AO voltage and the surfaces became more and more hydrophilic with increasing voltage. For <i>Escherichia coli</i> as Gram-negative and <i>Staphylococcus aureus</i> as Gram-positive, the counting of both bacteria on TiO<sub>2</sub> layers was less than ones on uncoated Ti45Nb. Moreover, the number of bacteria on the surface increased in direct proportion to the wettability result and increasing AO voltage. The AO layers produced at 25&#xa0;V indicated maximum inhibition ratio. They inhibited both bacteria at the ratio of 93.3% (<i>E. coli</i>) and 96.7% (<i>S. aureus</i>).</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Surface characterization, wettability and antimicrobial ability of anodic oxide TiO2 layers on Ti45Nb alloy

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年9月26日

查看全文
  • Salih Durdu,
  • Kadriye Özcan,
  • Selcuk Atasoy,
  • Yusuf Burak Bozkurt,
  • Halim Kovacı

摘要

Bacterial infections are among the foremost causes of morbidity and mortality on a global scale. In this study, TiO2 layers were performed on Ti45Nb alloys by anodic oxidation (AO) process with low voltages. Thus, the aim of this research is to investigate the surface properties, wettability and antimicrobial properties of TiO2 layers fabricated at low AO voltages on Ti45Nb alloy. The phase structures, morphologies and elemental amounts and distribution of the surfaces were characterized by XRD, Micro-Raman, SEM and EDX. The existence of anatase-TiO2 was verified on AO layer on Ti45Nb alloy. The wettability of AO layers improved with increasing AO voltage and the surfaces became more and more hydrophilic with increasing voltage. For Escherichia coli as Gram-negative and Staphylococcus aureus as Gram-positive, the counting of both bacteria on TiO2 layers was less than ones on uncoated Ti45Nb. Moreover, the number of bacteria on the surface increased in direct proportion to the wettability result and increasing AO voltage. The AO layers produced at 25 V indicated maximum inhibition ratio. They inhibited both bacteria at the ratio of 93.3% (E. coli) and 96.7% (S. aureus).