<p>Enamel prisms possess a unique microstructure, and their damage due to erosion is irreversible, making enamel restoration through non-invasive regeneration a significant challenge. This <i>in-vitro</i> study aimed to reconstruct the prism-like structure of enamel damaged by citric acid erosion through non-invasive biomimetic remineralization. Grape seed extract (GSE), combined with ethylenediaminetetraacetic acid (EDTA) and agarose hydrogel, was prepared via a hydrothermal technique. Additionally, a separate solution containing monoethanolamine (MEA) and potassium phosphate dibasic (K<sub>2</sub>HPO<sub>4</sub>) was prepared. Both solutions were applied as a treatment protocol for 30&#xa0;h on citric acid-eroded enamel surfaces. Three groups were compared: the control non-eroded enamel group (G0), the eroded non-treated enamel group (G1), and the treated enamel group (G2). The enamel surfaces were analyzed using atomic force microscopy (AFM), scanning electron microscopy coupled with energy dispersive X-ray analysis (SEM-EDX), and transmission electron microscopy (TEM). Significant topographic changes were observed in the G2 group compared to the G0 and G1 groups. AFM analysis revealed the formation of a new layer on the eroded surface as revealed by the increased arithmetical mean deviation of the roughness (Sa = 255.7 ± 40.61&#xa0;nm) and the smoother surface profile (Sku = 2.98 ± 0.53) of G2 compared to both G0 and G1. SEM examination showed the presence of uniform, prism-like, regenerative tissues, and EDX analysis confirmed the formation of hydroxyapatite (HAp) with a predominant calcium oxide (1.93 Ca/P molar ratio) phase on the treated enamel surface. TEM analysis indicated a crystal size of 12–15&#xa0;nm. In conclusion, the application of GSE/EDTA agarose hydrogel and MEA/ K<sub>2</sub>HPO<sub>4</sub> solution successfully repaired the eroded enamel surface, generating a uniform, prism-like enamel structure by providing the necessary inorganic mineral ions and the organic protein matrix template required for biomimetic remineralization.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Development of a novel Agarose/Nano-Hydroxyapatite/Grape seed extract hydrogel for biomimetic remineralization of demineralized human enamel (An In-Vitro Study)

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月18日

查看全文
  • Hanaa M. Elgamily,
  • Engie M. Safwat,
  • Ahmed M. Youssef

摘要

Enamel prisms possess a unique microstructure, and their damage due to erosion is irreversible, making enamel restoration through non-invasive regeneration a significant challenge. This in-vitro study aimed to reconstruct the prism-like structure of enamel damaged by citric acid erosion through non-invasive biomimetic remineralization. Grape seed extract (GSE), combined with ethylenediaminetetraacetic acid (EDTA) and agarose hydrogel, was prepared via a hydrothermal technique. Additionally, a separate solution containing monoethanolamine (MEA) and potassium phosphate dibasic (K2HPO4) was prepared. Both solutions were applied as a treatment protocol for 30 h on citric acid-eroded enamel surfaces. Three groups were compared: the control non-eroded enamel group (G0), the eroded non-treated enamel group (G1), and the treated enamel group (G2). The enamel surfaces were analyzed using atomic force microscopy (AFM), scanning electron microscopy coupled with energy dispersive X-ray analysis (SEM-EDX), and transmission electron microscopy (TEM). Significant topographic changes were observed in the G2 group compared to the G0 and G1 groups. AFM analysis revealed the formation of a new layer on the eroded surface as revealed by the increased arithmetical mean deviation of the roughness (Sa = 255.7 ± 40.61 nm) and the smoother surface profile (Sku = 2.98 ± 0.53) of G2 compared to both G0 and G1. SEM examination showed the presence of uniform, prism-like, regenerative tissues, and EDX analysis confirmed the formation of hydroxyapatite (HAp) with a predominant calcium oxide (1.93 Ca/P molar ratio) phase on the treated enamel surface. TEM analysis indicated a crystal size of 12–15 nm. In conclusion, the application of GSE/EDTA agarose hydrogel and MEA/ K2HPO4 solution successfully repaired the eroded enamel surface, generating a uniform, prism-like enamel structure by providing the necessary inorganic mineral ions and the organic protein matrix template required for biomimetic remineralization.