<p>The advancement of industrial technology has led to power modules facing challenges such as elevated temperatures, high voltages, and increased frequencies. The conventional epoxy resin (Ep) fails to satisfy the demands of high voltage and superior insulation. This study involved the synthesis of Ep resin/ AgNbO<sub>3</sub> nanocomposites aimed at addressing insulating flaws. AgNbO<sub>3</sub> was modified using the silane coupling agent KH550. The changes in the molecular chain after incorporating of unmodified and modified AgNbO<sub>3</sub> were evaluated through FTIR analysis. The SEM results indicate that following modification, AgNbO<sub>3</sub> particles are evenly distributed within the Ep resin matrix, demonstrating a lack of agglomeration. From thermal conductivity result it was found that modification of AgNbO<sub>3</sub> shows an enhancement of thermal conductivity, attributed to the reduction of interfacial phonon scattering and thermal resistance within the Ep resin. Additionally, the dielectric constant and dielectric loss in composites are greatly impacted by the addition of AgNbO<sub>3</sub>. According to the DC breakdown strength result, the addition of modified AgNbO<sub>3</sub> enhanced the process and caused deeper traps to form inside the bulk matrix. The distribution of trap energy levels is determined by Thermal Stimulated Depolarization Current (TSDC), which indicates that the incorporation of AgNbO<sub>3</sub> results in an increase in trap energy levels. Furthermore, the incorporation of 1 wt% AgNbO<sub>3</sub> particle into Ep resin has been observed to enhance the energy level of deep traps. After AgNbO<sub>3</sub> was added, DC Flashover in both air and vacuum significantly increased in comparison to pure Ep resin.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Enhancing the dielectric characteristics and DC flashover of epoxy resin composites by surface modification of AgNbO3 nano particles

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月2日

查看全文
  • Muhammad Zeeshan Khan,
  • Farooq Aslam,
  • Faisal Alsaif

摘要

The advancement of industrial technology has led to power modules facing challenges such as elevated temperatures, high voltages, and increased frequencies. The conventional epoxy resin (Ep) fails to satisfy the demands of high voltage and superior insulation. This study involved the synthesis of Ep resin/ AgNbO3 nanocomposites aimed at addressing insulating flaws. AgNbO3 was modified using the silane coupling agent KH550. The changes in the molecular chain after incorporating of unmodified and modified AgNbO3 were evaluated through FTIR analysis. The SEM results indicate that following modification, AgNbO3 particles are evenly distributed within the Ep resin matrix, demonstrating a lack of agglomeration. From thermal conductivity result it was found that modification of AgNbO3 shows an enhancement of thermal conductivity, attributed to the reduction of interfacial phonon scattering and thermal resistance within the Ep resin. Additionally, the dielectric constant and dielectric loss in composites are greatly impacted by the addition of AgNbO3. According to the DC breakdown strength result, the addition of modified AgNbO3 enhanced the process and caused deeper traps to form inside the bulk matrix. The distribution of trap energy levels is determined by Thermal Stimulated Depolarization Current (TSDC), which indicates that the incorporation of AgNbO3 results in an increase in trap energy levels. Furthermore, the incorporation of 1 wt% AgNbO3 particle into Ep resin has been observed to enhance the energy level of deep traps. After AgNbO3 was added, DC Flashover in both air and vacuum significantly increased in comparison to pure Ep resin.