<p>The mechanisms of 2-mercaptobenzothiazole (2-MBT) adsorption and corrosion inhibition on the aerospace AA2024 T3 aluminium alloy have been investigated using electrochemistry and advanced surface analyses. Electrochemical methods were used to measure the degree of corrosion protection in neutral chloride media, while advanced surface analysis techniques were employed to determine the interfacial interaction and inhibitor action mechanisms. It is shown that 2-MBT effectively inhibits corrosion of the alloy, reducing its susceptibility to corrosion attack and its corrosion rate. Surface analysis, including the use of ToF-SIMS 3-D chemical mapping, confirms 2-MBT adsorption on partially dealloyed intermetallic particles (IMPs) along with the presence of a thin 2-MBT layer on the top-most alloy surface. Chloride ions breakdown the native oxide film, allowing 2-MBT to adsorb on IMPs, thereby inhibiting further localized corrosion on these particles, while the 2-MBT layer on the surface protects the alloy matrix from surface oxidation.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Corrosion inhibition mechanisms of 2-mercaptobenzothiazole on AA2024 T3 aluminium alloy

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年8月3日

查看全文
  • Vishant Garg,
  • Maxime Magnan,
  • Sandrine Zanna,
  • Antoine Seyeux,
  • Frédéric Wiame,
  • Vincent Maurice,
  • Philippe Marcus

摘要

The mechanisms of 2-mercaptobenzothiazole (2-MBT) adsorption and corrosion inhibition on the aerospace AA2024 T3 aluminium alloy have been investigated using electrochemistry and advanced surface analyses. Electrochemical methods were used to measure the degree of corrosion protection in neutral chloride media, while advanced surface analysis techniques were employed to determine the interfacial interaction and inhibitor action mechanisms. It is shown that 2-MBT effectively inhibits corrosion of the alloy, reducing its susceptibility to corrosion attack and its corrosion rate. Surface analysis, including the use of ToF-SIMS 3-D chemical mapping, confirms 2-MBT adsorption on partially dealloyed intermetallic particles (IMPs) along with the presence of a thin 2-MBT layer on the top-most alloy surface. Chloride ions breakdown the native oxide film, allowing 2-MBT to adsorb on IMPs, thereby inhibiting further localized corrosion on these particles, while the 2-MBT layer on the surface protects the alloy matrix from surface oxidation.