<p>Metallic materials typically experience significant strength degradation at elevated temperatures. Traditional strengthening methods, which rely on thermally stable particle dispersion, exhibit limited effectiveness owing to the challenges in suppressing thermally activated dislocation motion. This work introduces a strategy for achieving exceptional high-temperature strength through a thermally stable nanoscale eutectic cellular network (ECN) enabled by additive manufacturing. A near-eutectic AlLaScZr alloy is developed for laser powder bed fusion, incorporating an Al-La nanoscale ECN and dense intracellular nanoprecipitates. This alloy demonstrates excellent printability and remarkable high-temperature yield strength above 0.6<i>T</i><sub>m</sub> (~250 MPa at 300 °C), outperforming conventional aluminium alloys by 2–5 times with minimal degradation after prolonged annealing. Compared with the conventional configuration of particle dispersion, the nanoscale ECN architecture enhances load-bearing capacity and strengthens aluminium by caging dislocation motion within ultrafine cells (~200 nm), effectively mitigating intrinsic high-temperature softening.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

High-temperature strength in an additively manufactured Al-based superalloy with stable nanoscale eutectic cellular networks

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年11月22日

查看全文
  • Siming Ma,
  • Zhe Chen,
  • Haixing Fang,
  • Gang Ji,
  • Mingliang Wang,
  • Yuchi Cui,
  • Yang Li,
  • Shengyi Zhong,
  • Han Chen,
  • Yi Wu,
  • Ying Zhou,
  • Shixin Nie,
  • Jian Lu

摘要

Metallic materials typically experience significant strength degradation at elevated temperatures. Traditional strengthening methods, which rely on thermally stable particle dispersion, exhibit limited effectiveness owing to the challenges in suppressing thermally activated dislocation motion. This work introduces a strategy for achieving exceptional high-temperature strength through a thermally stable nanoscale eutectic cellular network (ECN) enabled by additive manufacturing. A near-eutectic AlLaScZr alloy is developed for laser powder bed fusion, incorporating an Al-La nanoscale ECN and dense intracellular nanoprecipitates. This alloy demonstrates excellent printability and remarkable high-temperature yield strength above 0.6Tm (~250 MPa at 300 °C), outperforming conventional aluminium alloys by 2–5 times with minimal degradation after prolonged annealing. Compared with the conventional configuration of particle dispersion, the nanoscale ECN architecture enhances load-bearing capacity and strengthens aluminium by caging dislocation motion within ultrafine cells (~200 nm), effectively mitigating intrinsic high-temperature softening.