Scholarlink

<p>Boron enhances the hardenability of low-alloyed steel and reduces embrittlement at low temperatures, at parts-per-million concentration levels. Its effectiveness arises from segregation to grain boundaries (GBs)-planar defects between crystals-yet atomic-scale evidence remains limited. We addressed this gap by synthesizing GBs with controllable geometry and orientation, enabling reproducible comparison with and without boron segregation. Differential phase-contrast imaging directly reveals boron at iron GBs, and in-situ TEM heating (20 °C to 800 °C) allows us to track the dynamic evolution of GB structures. We found that boron segregation induces local structural changes and triggers GB phase transformations, as corroborated by calculated GB defect phase diagrams spanning broad ranges of carbon and boron content. Our findings not only bridge a gap in understanding the interplay between GB structure and chemistry but also lay the groundwork for targeted design and passivation strategies in steel, potentially transforming its resistance to hydrogen embrittlement, corrosion, and mechanical failure.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Boron triggers grain boundary structural transformation in steel

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年7月28日

查看全文
  • Xuyang Zhou,
  • Sourabh Kumar,
  • Siyuan Zhang,
  • Xinren Chen,
  • Baptiste Gault,
  • Gerhard Dehm,
  • Tilmann Hickel,
  • Dierk Raabe

摘要

Boron enhances the hardenability of low-alloyed steel and reduces embrittlement at low temperatures, at parts-per-million concentration levels. Its effectiveness arises from segregation to grain boundaries (GBs)-planar defects between crystals-yet atomic-scale evidence remains limited. We addressed this gap by synthesizing GBs with controllable geometry and orientation, enabling reproducible comparison with and without boron segregation. Differential phase-contrast imaging directly reveals boron at iron GBs, and in-situ TEM heating (20 °C to 800 °C) allows us to track the dynamic evolution of GB structures. We found that boron segregation induces local structural changes and triggers GB phase transformations, as corroborated by calculated GB defect phase diagrams spanning broad ranges of carbon and boron content. Our findings not only bridge a gap in understanding the interplay between GB structure and chemistry but also lay the groundwork for targeted design and passivation strategies in steel, potentially transforming its resistance to hydrogen embrittlement, corrosion, and mechanical failure.