<p>Nature uses fibrous structures for sensing and structural functions as observed in hairs, whiskers, stereocilia, spider silks, and hagfish slime thread skeins. Here, we demonstrate multi-nozzle printing of 3D hair arrays having freeform trajectories at a very high rate, with fiber diameters as fine as 1.5 µm, continuous lengths reaching tens of centimeters, and a wide range of materials with elastic moduli from 5 MPa to 3500 MPa. This is achieved via 3D printing by rapid solvent exchange in high yield stress micro granular gel, leading to radial solidification of the extruded polymer filament at a rate of 2.33 μm/s. This process extrudes filaments at 5 mm/s, which is 500,000 times faster than meniscus printing owing to the rapid solidification which prevents capillarity-induced fiber breakage. This study demonstrates the potential of 3D printing by rapid solvent exchange as a fast and scalable process for replicating natural fibrous structures for use in biomimetic functions.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Fast 3D printing of fine, continuous, and soft fibers via embedded solvent exchange

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年1月20日

查看全文
  • Wonsik Eom,
  • Mohammad Tanver Hossain,
  • Vidush Parasramka,
  • Jeongmin Kim,
  • Ryan W. Y. Siu,
  • Kate A. Sanders,
  • Dakota Piorkowski,
  • Andrew Lowe,
  • Hyun Gi Koh,
  • Michael F. L. De Volder,
  • Douglas S. Fudge,
  • Randy H. Ewoldt,
  • Sameh H. Tawfick

摘要

Nature uses fibrous structures for sensing and structural functions as observed in hairs, whiskers, stereocilia, spider silks, and hagfish slime thread skeins. Here, we demonstrate multi-nozzle printing of 3D hair arrays having freeform trajectories at a very high rate, with fiber diameters as fine as 1.5 µm, continuous lengths reaching tens of centimeters, and a wide range of materials with elastic moduli from 5 MPa to 3500 MPa. This is achieved via 3D printing by rapid solvent exchange in high yield stress micro granular gel, leading to radial solidification of the extruded polymer filament at a rate of 2.33 μm/s. This process extrudes filaments at 5 mm/s, which is 500,000 times faster than meniscus printing owing to the rapid solidification which prevents capillarity-induced fiber breakage. This study demonstrates the potential of 3D printing by rapid solvent exchange as a fast and scalable process for replicating natural fibrous structures for use in biomimetic functions.