Carrier-phonon decoupling in perovskite thermoelectrics via entropy engineering
摘要
Thermoelectrics converting heat and electricity directly attract broad attentions. To enhance the thermoelectric figure of merit, zT, one of the key points is to decouple the carrier-phonon transport. Here, we propose an entropy engineering strategy to realize the carrier-phonon decoupling in the typical SrTiO3-based perovskite thermoelectrics. By high-entropy design, the lattice thermal conductivity could be reduced nearly to the amorphous limit, 1.25 W m−1 K−1. Simultaneously, entropy engineering can tune the Ti displacement, improving the weighted mobility to 65 cm2 V−1 s−1. Such carrier-phonon decoupling behaviors enable the greatly enhanced μW/κL of ~5.2 × 103 cm3 K J−1 V−1. The measured maximum zT of 0.24 at 488 K and the estimated zT of ~0.8 at 1173 K in (Sr0.2Ba0.2Ca0.2Pb0.2La0.2)TiO3 film are among the best of n-type thermoelectric oxides. These results reveal that the entropy engineering may be a promising strategy to decouple the carrier-phonon transport and achieve higher zT in thermoelectrics.