<p>The exploration is carried out to estimate the properties of glass/epoxy (GE) composites under thermal conditioning environment with and without embedding of TiO<sub>2</sub> nanoparticles in the epoxy matrix. Evaluation of flexural strength and flexural modulus of the GE composites was carried out at different loading rates i.e. at 1, 10, 100, 500, and 1000&#xa0;mm/min and at different test conditions. The polymer phase was reformed using different concentration (0.1 wt%, 0.3 wt% and 0.5 wt%) of nano-TiO<sub>2</sub> filler. The different sets of specimens were thermally conditioned at a temperature range of + 60&#xa0;°C for duration of 12&#xa0;h and same specimens again treated at – 60&#xa0;°C for 12&#xa0;h. This thermal shock conditioning was carried out for a period of 30 days. The unconditioned specimens follow an increasing trend in flexural strength with increase in the loading rates. But for conditioned specimens, the flexural strength increases up to 10&#xa0;mm/min and after further increase in loading rates the strength decreases for all nano-TiO<sub>2</sub> concentration. Maximum strength for flexural tests was obtained for 0.1 wt% nano-TiO<sub>2</sub> embedded GE composites for both conditioned and unconditioned composite specimens. The flexural strength was better in case of thermal conditioned specimen as compared to that of unconditioned specimen. Fractography analysis of failed composite specimens was carried out using scanning electron microscopy (SEM) and glass transition temperature was measured using differential scanning calorimetry (DSC). The developed nano-TiO₂ reinforced GE composites, with enhanced mechanical and thermal steadiness under severe thermal cycling and dynamic loading, are predominantly appropriate for aerospace structural components, UAV housings, radome panels, fairings, and other high-performance lightweight applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Characterization of mechanical, thermal, and morphological properties of nano-TiO₂ doped glass fiber/epoxy composites under severe thermal cycling and dynamic loading conditions for aerospace applications

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年12月22日

查看全文
  • Chinmaya Prasad Mohanty,
  • Alok Behera,
  • Nishant Tiwari,
  • Gunji Balamurali,
  • Senthil Kumaran Selvaraj,
  • Amborish Banerjee,
  • Kishore Kumar Mahato

摘要

The exploration is carried out to estimate the properties of glass/epoxy (GE) composites under thermal conditioning environment with and without embedding of TiO2 nanoparticles in the epoxy matrix. Evaluation of flexural strength and flexural modulus of the GE composites was carried out at different loading rates i.e. at 1, 10, 100, 500, and 1000 mm/min and at different test conditions. The polymer phase was reformed using different concentration (0.1 wt%, 0.3 wt% and 0.5 wt%) of nano-TiO2 filler. The different sets of specimens were thermally conditioned at a temperature range of + 60 °C for duration of 12 h and same specimens again treated at – 60 °C for 12 h. This thermal shock conditioning was carried out for a period of 30 days. The unconditioned specimens follow an increasing trend in flexural strength with increase in the loading rates. But for conditioned specimens, the flexural strength increases up to 10 mm/min and after further increase in loading rates the strength decreases for all nano-TiO2 concentration. Maximum strength for flexural tests was obtained for 0.1 wt% nano-TiO2 embedded GE composites for both conditioned and unconditioned composite specimens. The flexural strength was better in case of thermal conditioned specimen as compared to that of unconditioned specimen. Fractography analysis of failed composite specimens was carried out using scanning electron microscopy (SEM) and glass transition temperature was measured using differential scanning calorimetry (DSC). The developed nano-TiO₂ reinforced GE composites, with enhanced mechanical and thermal steadiness under severe thermal cycling and dynamic loading, are predominantly appropriate for aerospace structural components, UAV housings, radome panels, fairings, and other high-performance lightweight applications.