<p>To optimize the electrochemical properties of Ni-rich cathode materials, CPAN@SC-NCM811 is prepared via surface modification of single-crystalline LiNi<sub>0.8</sub>Co<sub>0.1</sub>Mn<sub>0.1</sub>O<sub>2</sub> cathode material by adding 1, 2 and 3&#xa0;wt.% of polyacrylonitrile, respectively. Significantly, the results obtained from X-ray diffraction&#xa0;(XRD), Fourier transform infrared spectroscopy&#xa0;(FTIR), X-ray photoelectron spectroscopy&#xa0;(XPS), field emission scanning electron microscopy&#xa0;(FESEM), and transmission electron microscopy&#xa0;(TEM) verify the successful synthesis of CPAN@SC-NCM811 cathode, which exhibits better electrochemical properties compared to SC-NMC811. After thorough milling and calcination of 2&#xa0;wt.% polyacrylonitrile with SC-NCM811, the initial discharge specific capacity of prepared S2 sample is 197.7&#xa0;mAh&#xa0;g<sup>−1</sup> and the capacity retention reached 89.2% after 100 cycles at a rate of 1.0&#xa0;C. Furthermore, the S2 sample exhibits superior rate performance compared to the other three samples, in which these superior electrochemical properties are largely attributed to the optimal ratio of conductive cyclized polyacrylonitrile coatings. Overall, this work offers guidelines for modifying the surface of SC-NCM811 cathode materials for lithium-ion batteries with exceptional cycling and rate performance.</p> Graphical abstract <p>Preparation schematic of the CPAN@SC-NCM811 cathode materials and the corresponding cycling performance of the assembled coin cells</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Optimization of conductive cyclized polyacrylonitrile content to enhance the structural stability of single-crystal LiNi0.8Co0.1Mn0.1O2 cathode materials for lithium-ion batteries

  • 期刊论文

  • 发表日期：

    2025年1月31日

查看全文
  • Minyue Wen,
  • Sheng Wang,
  • Jiawen Wang,
  • Jiafu Yu,
  • Shuaihao Li,
  • Qiuyu Zeng

摘要

To optimize the electrochemical properties of Ni-rich cathode materials, CPAN@SC-NCM811 is prepared via surface modification of single-crystalline LiNi0.8Co0.1Mn0.1O2 cathode material by adding 1, 2 and 3 wt.% of polyacrylonitrile, respectively. Significantly, the results obtained from X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), X-ray photoelectron spectroscopy (XPS), field emission scanning electron microscopy (FESEM), and transmission electron microscopy (TEM) verify the successful synthesis of CPAN@SC-NCM811 cathode, which exhibits better electrochemical properties compared to SC-NMC811. After thorough milling and calcination of 2 wt.% polyacrylonitrile with SC-NCM811, the initial discharge specific capacity of prepared S2 sample is 197.7 mAh g−1 and the capacity retention reached 89.2% after 100 cycles at a rate of 1.0 C. Furthermore, the S2 sample exhibits superior rate performance compared to the other three samples, in which these superior electrochemical properties are largely attributed to the optimal ratio of conductive cyclized polyacrylonitrile coatings. Overall, this work offers guidelines for modifying the surface of SC-NCM811 cathode materials for lithium-ion batteries with exceptional cycling and rate performance.

Graphical abstract

Preparation schematic of the CPAN@SC-NCM811 cathode materials and the corresponding cycling performance of the assembled coin cells