<p>Fatigue failure of welded joints is a performance factor of structural parts under dynamic load, and the effective evaluation of its life is always the key to the service ability of structures. The fatigue failure process of welded joints is complicated because of the non-uniformity of microstructure and asymmetry of structure. This study utilized ultrasonic C-scan imaging for non-destructive testing of the internal connection states of resistance projection welding (RPW). The connection state of RPW before, during and after fatigue test and the characteristic change of ultrasonic detection image were compared. With the occurrence of fatigue failure behavior, the area representing the fusion connection region in the ultrasonic C-scan image changes. The area of the molten connection zone in the ultrasonic images can quantitatively evaluate the fatigue limit of stainless steel RPW joints, providing an effective method for assessing fatigue life in practical engineering applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Study on ultrasonic evaluation of connection state and service performance of resistance projection welding joints

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年4月18日

查看全文
  • Zhenzhen Duan,
  • Xueshan Zhao,
  • Guanghao Zhou,
  • Kunning Jia,
  • Xiaopeng Gu,
  • Ting Ma

摘要

Fatigue failure of welded joints is a performance factor of structural parts under dynamic load, and the effective evaluation of its life is always the key to the service ability of structures. The fatigue failure process of welded joints is complicated because of the non-uniformity of microstructure and asymmetry of structure. This study utilized ultrasonic C-scan imaging for non-destructive testing of the internal connection states of resistance projection welding (RPW). The connection state of RPW before, during and after fatigue test and the characteristic change of ultrasonic detection image were compared. With the occurrence of fatigue failure behavior, the area representing the fusion connection region in the ultrasonic C-scan image changes. The area of the molten connection zone in the ultrasonic images can quantitatively evaluate the fatigue limit of stainless steel RPW joints, providing an effective method for assessing fatigue life in practical engineering applications.