<p>This article summarizes the electron density analysis of Bi<sub>0.95</sub>Ca<sub>0.05</sub>Fe<sub>1-x</sub>Nb<sub>x</sub>O<sub>3</sub>(x = 0.02, 0.04, 0.06) samples that correlate the microstructural, optical, and magnetic properties prepared using the sol–gel method. The X-ray diffraction patterns of the synthesized samples reveal that the subtle peaks synchronize primarily with the R3c phase in these samples. The electron density and bonding characteristics of polycrystalline Bi<sub>0.95</sub>Ca<sub>0.05</sub>Fe<sub>1-x</sub>Nb<sub>x</sub>O<sub>3</sub>(x = 0.02, 0.04, 0.06) samples were analysed using the Maximum Entropy Method. The two-dimensional contour map reveals that the covalent bonding distance between Bi/Ca-O and the ionic bonding distance between Fe/Nb–O converge well in the Bi<sub>0.95</sub>Ca<sub>0.05</sub>Fe<sub>0.96</sub>Nb<sub>0.04</sub>O<sub>3</sub> sample and correlate with optical and magnetic properties. The bandgap energies of Bi<sub>0.95</sub>Ca<sub>0.05</sub>Fe<sub>1-x</sub>Nb<sub>x</sub>O<sub>3</sub>(x = 0.02, 0.04, 0.06) are observed to be 1.78&#xa0;eV, 1.97&#xa0;eV and 1.72&#xa0;eV respectively. The surface roughness shows an increasing trend in transmission spectra. As a result, the optical density and hence the refractive index reduce in all the samples. The maximum magnetization of Bi<sub>0.95</sub>Ca<sub>0.05</sub>Fe<sub>0.96</sub>Nb<sub>0.04</sub>O<sub>3</sub> is considerably enhanced compared to other samples.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Electron density analysis of Bi0.95Ca0.05Fe1-xNbxO3(x = 0.02, 0.04, 0.06) samples that correlate microstructural, optical and magnetic properties

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年4月12日

查看全文
  • A. Sutha,
  • M. Mohammed Sheik Sirajudeen,
  • R. Rajesh,
  • I. B. Shameem Banu

摘要

This article summarizes the electron density analysis of Bi0.95Ca0.05Fe1-xNbxO3(x = 0.02, 0.04, 0.06) samples that correlate the microstructural, optical, and magnetic properties prepared using the sol–gel method. The X-ray diffraction patterns of the synthesized samples reveal that the subtle peaks synchronize primarily with the R3c phase in these samples. The electron density and bonding characteristics of polycrystalline Bi0.95Ca0.05Fe1-xNbxO3(x = 0.02, 0.04, 0.06) samples were analysed using the Maximum Entropy Method. The two-dimensional contour map reveals that the covalent bonding distance between Bi/Ca-O and the ionic bonding distance between Fe/Nb–O converge well in the Bi0.95Ca0.05Fe0.96Nb0.04O3 sample and correlate with optical and magnetic properties. The bandgap energies of Bi0.95Ca0.05Fe1-xNbxO3(x = 0.02, 0.04, 0.06) are observed to be 1.78 eV, 1.97 eV and 1.72 eV respectively. The surface roughness shows an increasing trend in transmission spectra. As a result, the optical density and hence the refractive index reduce in all the samples. The maximum magnetization of Bi0.95Ca0.05Fe0.96Nb0.04O3 is considerably enhanced compared to other samples.