High-temperature wear resistance, oxidation resistance and melting loss resistance of plasma cladded Co06–Ni60A composite coating for coppery blast furnace tuyere
摘要
To improve the high-temperature service properties of coppery tuyere, Co06 coating with a Ni60A interlayer was prepared on copper by plasma cladding. Ni60A interlayer acted as a bridge to promote the element diffusion, thus achieving metallurgical bonding. Due to the strengthening effect of γ-Co, Cr23C6 and Cr7C3 phases, the wear resistance of Co06–Ni60A coating was much higher than that of copper substrate. As the temperature increased, the wear resistance of coating decreased first and then increased. The coating exhibited better wear resistance at 600 °C due to the oxidation wear mechanism. Compared with copper substrate and Ni60A, the oxidation resistance of Co06 was increased by 6.0 and 1.9 times, respectively. For melting loss resistance, Co06–Ni60A coating was superior to Ni60A single-layer coating, but the molten iron can still form a micro-metallurgical bonding with the coating surface