<p>The conventional sintered W-Ni-Fe alloy encounters challenges in achieving both high strength and plasticity simultaneously, primarily due to its inadequate organizational compatibility. To address this issue, we developed a novel approach combining in situ freeze-drying and straightforward liquid-phase sintering techniques to effectively control the microstructure of 93W-4.9Ni-2.1Fe alloys. The corresponding W-Ni-Fe alloy in this work simultaneously takes into account ultrafine W grains (28.3 µm), low W-W connectivity (CW-W = 0.31), and suitable γ phase volume fraction (20.2%), which is currently difficult for traditional W-Ni-Fe alloys to achieve. The minute dimensions of nanopowder play a crucial role in inhibiting Ostwald ripening and facilitating W grain refinement. Additionally, the extensive surface area of nanopowder enhances capillary penetration, leading to effective homogenization of high γ phase volume. As a result, the freeze-dried W-Ni-Fe alloy simultaneously achieves high strength (1010 MPa) and high plasticity (31%), which provides a new insight for the further development of W-Ni-Fe alloy industries.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

A strategy for optimizing microstructure to simultaneously improve the strength and plasticity of W-Ni-Fe alloy

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年10月16日

查看全文
  • Chongji Wu,
  • Lu Yang,
  • Zhu Qian,
  • Zupeng Yan,
  • Xia Sun,
  • Weiqiang Hu,
  • Zongqing Ma

摘要

The conventional sintered W-Ni-Fe alloy encounters challenges in achieving both high strength and plasticity simultaneously, primarily due to its inadequate organizational compatibility. To address this issue, we developed a novel approach combining in situ freeze-drying and straightforward liquid-phase sintering techniques to effectively control the microstructure of 93W-4.9Ni-2.1Fe alloys. The corresponding W-Ni-Fe alloy in this work simultaneously takes into account ultrafine W grains (28.3 µm), low W-W connectivity (CW-W = 0.31), and suitable γ phase volume fraction (20.2%), which is currently difficult for traditional W-Ni-Fe alloys to achieve. The minute dimensions of nanopowder play a crucial role in inhibiting Ostwald ripening and facilitating W grain refinement. Additionally, the extensive surface area of nanopowder enhances capillary penetration, leading to effective homogenization of high γ phase volume. As a result, the freeze-dried W-Ni-Fe alloy simultaneously achieves high strength (1010 MPa) and high plasticity (31%), which provides a new insight for the further development of W-Ni-Fe alloy industries.