<p>In this research, carbon hollow spheres (CSs) were synthesized by carbonizing polysaccharide shells deposited on silica spheres as hard templates to obtain graphenic carbon shells. Melamine-based covalent organic framework (COF) 3D nanostructures (NSs) were synthesized onto the surface of CSs to enhance their compatibility with the epoxy matrix and their capacity for encapsulating zinc cations and green L-glutamate (ZG) as corrosion inhibitors. Corrosion protection studies of the CS@ZG-COF extract showed an increase in the total impedance of immersed steel from 2298.5 to 14,502.2 Ω cm<sup>2</sup> after 24 h, compared to the control solution. The potentiodynamic polarization (PP) test revealed an inhibition efficiency of 82.43% for the CS@ZG-COF extract. The EP/CS@ZG-COF coating demonstrated exceptional self-healing ability, corrosion protection, and barrier properties, forming a robust and uniform protective layer due to the release of encapsulated ZG complexes, which enhanced its electrochemical performance compared to other tested coatings. Furthermore, the incorporation of CS@ZG-COF NSs increased both dry and wet adhesion strength of the epoxy coatings, while the cathodic delamination radius was reduced from 7.6 to 4.4 mm in their presence.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Covalent organic framework (COF)-enhanced carbon hollow sphere (CS): a novel nano-porous material for robust epoxy composite coating intelligent corrosion protection

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年8月16日

查看全文
  • Ali Davarpanah,
  • Seyyed Arash Haddadi,
  • Mohammad Ramezanzadeh,
  • Bahram Ramezanzadeh,
  • Tizazu H. Mekonnen

摘要

In this research, carbon hollow spheres (CSs) were synthesized by carbonizing polysaccharide shells deposited on silica spheres as hard templates to obtain graphenic carbon shells. Melamine-based covalent organic framework (COF) 3D nanostructures (NSs) were synthesized onto the surface of CSs to enhance their compatibility with the epoxy matrix and their capacity for encapsulating zinc cations and green L-glutamate (ZG) as corrosion inhibitors. Corrosion protection studies of the CS@ZG-COF extract showed an increase in the total impedance of immersed steel from 2298.5 to 14,502.2 Ω cm2 after 24 h, compared to the control solution. The potentiodynamic polarization (PP) test revealed an inhibition efficiency of 82.43% for the CS@ZG-COF extract. The EP/CS@ZG-COF coating demonstrated exceptional self-healing ability, corrosion protection, and barrier properties, forming a robust and uniform protective layer due to the release of encapsulated ZG complexes, which enhanced its electrochemical performance compared to other tested coatings. Furthermore, the incorporation of CS@ZG-COF NSs increased both dry and wet adhesion strength of the epoxy coatings, while the cathodic delamination radius was reduced from 7.6 to 4.4 mm in their presence.