Effect of Bimodal Quasicrystal Phase on the Dynamic Recrystallization of Mg–Zn–Gd Alloy during High-Pressure Torsion

The Mg–Zn–Gd alloy with quasicrystal icosahedral phase was processed by high-pressure torsion (HPT). The effect of bimodal I-phase on the dynamic recrystallization was analyzed by transmission electron microscopy. The results showed that the block I-phase can stimulate obvious particle-stimulated nucleation and dynamic recrystallization (DRX) grains were preferentially formed after HPT for 5 turns, while the granular I-phase only promoted the generation of sub-grains. The orientation relationship was determined as twofold//[12 \(\overline{1 }\) $\overline{1}$ 0] and fivefold//(0002)_Mg. Moreover, after HPT for 9 turns, the DRX grains induced by block I-phase appeared to grow up and coarsened. Compared with block I-phase, the grains induced by granular I-phase presented much smaller size and distributed more homogeneous due to the strong pinning effect.