<p>The article is focused on examining the optical properties of the polymer binder based on polymethylphenylsiloxane varnish. The varnish was modified with SiO<sub>2</sub> nanoparticles of various concentrations. The diffuse reflectance and transmittance spectra within 200 to 2500&#xa0;nm were measured in vacuum (2·10<sup>–6</sup>&#xa0;Torr) before and after irradiation with accelerated electrons (in situ, E = 30&#xa0;keV, F = 2·10<sup>16</sup>&#xa0;cm<sup>−2</sup>). Additionally, solar absorptance was calculated and the shift in the optical absorption edge was established. The post-modification increase in reflectance has been recorded in the UV and visible regions. In the near-IR region, the reflectance coefficient was found to increase or decrease in accordance with the nanoparticles’ concentration. The irradiation of the varnish samples with electrons leads to the formation of the absorption band within 200 to 600&#xa0;nm. The nanoparticle-based modification leads to the decrease in the intensity of the induced absorption band. The nanoparticle concentration values suitable for the varnish radiation stability were established. Additionally, it was confirmed that the modification of varnish with SiO<sub>2</sub> nanoparticles provides 1.6 fold increase in its radiation stability when exposed to radiation.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Optical Properties and Radiation Stability of Polymethylphenylsiloxane Varnish Modified with SiO2 Nanoparticles

  • 期刊论文

  • 发表日期：

    2025年7月16日

查看全文
  • Mikhail M. Mikhailov,
  • Vladimir A. Goronchko,
  • Alexey N. Lapin,
  • Semyon A. Yuryev,
  • Dmitriy S. Fedosov

摘要

The article is focused on examining the optical properties of the polymer binder based on polymethylphenylsiloxane varnish. The varnish was modified with SiO2 nanoparticles of various concentrations. The diffuse reflectance and transmittance spectra within 200 to 2500 nm were measured in vacuum (2·10–6 Torr) before and after irradiation with accelerated electrons (in situ, E = 30 keV, F = 2·1016 cm−2). Additionally, solar absorptance was calculated and the shift in the optical absorption edge was established. The post-modification increase in reflectance has been recorded in the UV and visible regions. In the near-IR region, the reflectance coefficient was found to increase or decrease in accordance with the nanoparticles’ concentration. The irradiation of the varnish samples with electrons leads to the formation of the absorption band within 200 to 600 nm. The nanoparticle-based modification leads to the decrease in the intensity of the induced absorption band. The nanoparticle concentration values suitable for the varnish radiation stability were established. Additionally, it was confirmed that the modification of varnish with SiO2 nanoparticles provides 1.6 fold increase in its radiation stability when exposed to radiation.