<p>The extreme removal of SiO<sub>2</sub> and MnO inclusions in 304 stainless steel in supergravity fields was investigated using an in-house high-temperature supergravity equipment. The influences of the gravity coefficient and separation time on the removal efficiency of the inclusions were studied. After supergravity treatment, the inclusions migrated to the top of the sample and formed large aggregates. Meanwhile, the lower part of the sample was purified considerably and appeared significantly cleaner than the raw material. At the gravity coefficient of 500 and separation time of 600 s, the total oxygen content at the bottom of the sample (position E) decreased from 240 to 28 ppm. This corresponded to a total oxygen removal rate of 88.33%. The volume fraction and number density of inclusions exhibited a gradient distribution along the supergravity direction, with values of 8.5% and 106 mm<sup>−2</sup> at the top of the sample (position A) and 0.06% and 22 mm<sup>−2</sup> at its bottom.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Extreme removal of fine inclusions from 304 stainless steel via high-temperature supergravity fields

  • 期刊论文

  • 发表日期：

    2025年10月10日

查看全文
  • Shuai Zhang,
  • Lei Guo,
  • Zhancheng Guo

摘要

The extreme removal of SiO2 and MnO inclusions in 304 stainless steel in supergravity fields was investigated using an in-house high-temperature supergravity equipment. The influences of the gravity coefficient and separation time on the removal efficiency of the inclusions were studied. After supergravity treatment, the inclusions migrated to the top of the sample and formed large aggregates. Meanwhile, the lower part of the sample was purified considerably and appeared significantly cleaner than the raw material. At the gravity coefficient of 500 and separation time of 600 s, the total oxygen content at the bottom of the sample (position E) decreased from 240 to 28 ppm. This corresponded to a total oxygen removal rate of 88.33%. The volume fraction and number density of inclusions exhibited a gradient distribution along the supergravity direction, with values of 8.5% and 106 mm−2 at the top of the sample (position A) and 0.06% and 22 mm−2 at its bottom.