<p>In this study, we investigated the peculiar flow behavior during the isothermal deformation of a novel TiAl composition at 1200&#xa0;°C and 1300&#xa0;°C under high strain rate conditions using Gleeble<sup>®</sup> Thermal-Mechanical Simulators. The initial yield-point phenomenon, resembling strain hardening at both temperatures, is attributed to the remnant lamellar microstructure. Secondary hardening at 1200 ℃ is caused by dislocation accumulation at the grain boundaries of the α phase, without the formation of dynamically recrystallized γ lamellar grains. In-grain misorientation axes analysis revealed a shift in the dominant deformation slip mode of the α phase from the prismatic slip system to a combined prismatic and basal slip system. The disappearance of γ lamellar laths after the first strain hardening and during secondary hardening is likely initiated by a deformation-induced γ→α phase transition within the γ phase matrix by the extended dislocation with intrinsic stacking faults and occurred simultaneously in the whole γ lamellae.</p> Graphical Abstract <p></p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Investigation of the Peculiar Stress Flow Behavior of a Novel TiAl Alloy under High Strain Rate Conditions

  • 期刊论文

  • 发表日期：

    2025年1月7日

查看全文
  • Ji-Sung Park,
  • Min-Sik Kim,
  • Jong-Woo Won,
  • Seong-Woong Kim,
  • Seong-Hoon Yi

摘要

In this study, we investigated the peculiar flow behavior during the isothermal deformation of a novel TiAl composition at 1200 °C and 1300 °C under high strain rate conditions using Gleeble® Thermal-Mechanical Simulators. The initial yield-point phenomenon, resembling strain hardening at both temperatures, is attributed to the remnant lamellar microstructure. Secondary hardening at 1200 ℃ is caused by dislocation accumulation at the grain boundaries of the α phase, without the formation of dynamically recrystallized γ lamellar grains. In-grain misorientation axes analysis revealed a shift in the dominant deformation slip mode of the α phase from the prismatic slip system to a combined prismatic and basal slip system. The disappearance of γ lamellar laths after the first strain hardening and during secondary hardening is likely initiated by a deformation-induced γ→α phase transition within the γ phase matrix by the extended dislocation with intrinsic stacking faults and occurred simultaneously in the whole γ lamellae.

Graphical Abstract