<p>A novel spinning method that integrates electrospun nanofiber strips into yarn structures has been developed to produce multifunctional yarns. The resulting yarn exhibited a core-sheath structure, with a core composed of tannic acid-modified magnesium hydroxide/thermoplastic polyurethane (TA@MH/TPU) nanofiber strip, sheathed by either pure cotton or cotton/sodium alginate blended fibers. The TA modification improved the dispersion of MH within the TPU matrix, leading to enhanced membrane strength compared to unmodified MH/TPU at equal loadings. The film containing 7% TA@MH/TPU demonstrated optimal mechanical properties (breaking strength of 1.43&#xa0;MPa, elongation of 122.93%), flame retardancy (limiting oxygen index of 27.1%), and antibacterial efficacy killing ratios of 80.87% against <i>E. coli</i> and 85.07% against <i>S. aureus</i>. Yarns fabricated with this film, the TA@MH/TPU-cotton (CMSCY) retained the antibacterial functionality (67.48% against <i>E. coli</i> and 79.05% against <i>S. aureus</i>), and the TA@MH/TPU-cotton/sodium alginate (C/SAMSCY) achieved the flame retardancy with a limiting oxygen index of 27.8%. Notably, the CMSCY yarn showed a high tensile strength of 1.53&#xa0;MPa, which was 15 times that of the TA@MH/TPU nanofiber film, addressing the application limitations of nanofiber membranes caused by their low mechanical strength. Given that electrospun membranes can be readily functionalized, this spinning method offers a promising strategy for producing composite yarns, particularly for developing multifunctional textile fabrics.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Preparation of TA@Mg(OH)2/TPU Nanofiber Film and Its Composite Yarns with Flame Retardancy, Antibacterial and Mechanical Improvement

  • 期刊论文

  • 发表日期：

    2025年10月8日

查看全文
  • Shuo Zhang,
  • Mengyao Guo,
  • Jiaqing Wu,
  • Ying Wang,
  • Xin Zhang

摘要

A novel spinning method that integrates electrospun nanofiber strips into yarn structures has been developed to produce multifunctional yarns. The resulting yarn exhibited a core-sheath structure, with a core composed of tannic acid-modified magnesium hydroxide/thermoplastic polyurethane (TA@MH/TPU) nanofiber strip, sheathed by either pure cotton or cotton/sodium alginate blended fibers. The TA modification improved the dispersion of MH within the TPU matrix, leading to enhanced membrane strength compared to unmodified MH/TPU at equal loadings. The film containing 7% TA@MH/TPU demonstrated optimal mechanical properties (breaking strength of 1.43 MPa, elongation of 122.93%), flame retardancy (limiting oxygen index of 27.1%), and antibacterial efficacy killing ratios of 80.87% against E. coli and 85.07% against S. aureus. Yarns fabricated with this film, the TA@MH/TPU-cotton (CMSCY) retained the antibacterial functionality (67.48% against E. coli and 79.05% against S. aureus), and the TA@MH/TPU-cotton/sodium alginate (C/SAMSCY) achieved the flame retardancy with a limiting oxygen index of 27.8%. Notably, the CMSCY yarn showed a high tensile strength of 1.53 MPa, which was 15 times that of the TA@MH/TPU nanofiber film, addressing the application limitations of nanofiber membranes caused by their low mechanical strength. Given that electrospun membranes can be readily functionalized, this spinning method offers a promising strategy for producing composite yarns, particularly for developing multifunctional textile fabrics.