<p>This study developed a CECS/ZnO-functionalized cotton fiber sheets as a single-use filter layer for face masks, with enhanced antibacterial and photocatalytic properties. Cotton fiber sheets were modified with zinc oxide nanoparticles (ZnO NPs) using a dip-coating method, with and without carboxyethyl chitosan (CECS) as a binder and stabilizing agent. The fiber sheets were treated with 0.1, 0.3, and 0.5&#xa0;M Zn(NO<sub>3</sub>)<sub>2</sub> solutions, followed by hydrothermal synthesis in NH<sub>4</sub>OH (Zn:NH<sub>4</sub>OH = 1:2) at 100&#xa0;°C for 1&#xa0;h. The study successfully demonstrated ZnO NPs formation on cotton sheets, producing ZnO-immobilized cotton sheets (Cf/Zn). Higher Zn<sup>2</sup>⁺ concentrations promoted greater nucleation of ZnO nanoparticles. However, they also caused particle agglomeration, which reduced the surface area and weakened ZnO adhesion to the cotton fibers. This presents a significant challenge in achieving a uniform nanoparticle distribution. However, the introduction of carboxyethyl chitosan (CECS) (Cf/CECS/Zn) as a binder and stabilizer represents a novel approach that showed a superior ZnO adhesion, better particle distribution, and higher Zn content than untreated Cf/Zn. Among the samples, Cf/CECS/Zn0.1 exhibited the highest Zn content (154&#xa0;ppm), the highest antibacterial zone diameter (29.39&#xa0;mm), and the most effective photocatalytic activity (65.66%). While both Cf/Zn and Cf/CECS/Zn demonstrated antibacterial activity against <i>S. aureus</i>, Cf/CECS/Zn0.1 showed superior performance, with low cytotoxicity confirmed by Vero cell viability tests. The treated fibers also displayed enhanced hydrophobic and photocatalytic properties. These results demonstrate the potential of CECS-modified ZnO-immobilized cotton sheets for advanced healthcare filtration applications, offering enhanced antibacterial, photocatalytic, and non-toxic properties.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Enhanced Photocatalytic and Biological Properties of Cellulose Cotton Fabric Coated with Carboxyethyl Chitosan/Zinc Oxide Bio-nanocomposite

  • 期刊论文

  • 发表日期：

    2025年7月14日

查看全文
  • Mutiara Ayu,
  • Punnama Siriphannon,
  • Pathavuth Monvisade

摘要

This study developed a CECS/ZnO-functionalized cotton fiber sheets as a single-use filter layer for face masks, with enhanced antibacterial and photocatalytic properties. Cotton fiber sheets were modified with zinc oxide nanoparticles (ZnO NPs) using a dip-coating method, with and without carboxyethyl chitosan (CECS) as a binder and stabilizing agent. The fiber sheets were treated with 0.1, 0.3, and 0.5 M Zn(NO3)2 solutions, followed by hydrothermal synthesis in NH4OH (Zn:NH4OH = 1:2) at 100 °C for 1 h. The study successfully demonstrated ZnO NPs formation on cotton sheets, producing ZnO-immobilized cotton sheets (Cf/Zn). Higher Zn2⁺ concentrations promoted greater nucleation of ZnO nanoparticles. However, they also caused particle agglomeration, which reduced the surface area and weakened ZnO adhesion to the cotton fibers. This presents a significant challenge in achieving a uniform nanoparticle distribution. However, the introduction of carboxyethyl chitosan (CECS) (Cf/CECS/Zn) as a binder and stabilizer represents a novel approach that showed a superior ZnO adhesion, better particle distribution, and higher Zn content than untreated Cf/Zn. Among the samples, Cf/CECS/Zn0.1 exhibited the highest Zn content (154 ppm), the highest antibacterial zone diameter (29.39 mm), and the most effective photocatalytic activity (65.66%). While both Cf/Zn and Cf/CECS/Zn demonstrated antibacterial activity against S. aureus, Cf/CECS/Zn0.1 showed superior performance, with low cytotoxicity confirmed by Vero cell viability tests. The treated fibers also displayed enhanced hydrophobic and photocatalytic properties. These results demonstrate the potential of CECS-modified ZnO-immobilized cotton sheets for advanced healthcare filtration applications, offering enhanced antibacterial, photocatalytic, and non-toxic properties.