<p>With the rapid development of cutting-edge electrical equipment and electrical systems, it is of great significance to develop advanced polymeric insulating paper with high breakdown strength under a high-temperature environment. In this paper, aramid nanofibers (ANF) and original poly(m-phenylene isophthalamide) (PMIA) paper were utilized to construct ANF/PMIA/ANF composite papers with sandwich structure. On account of the reduced surface roughness of the original PMIA paper, the high breakdown strength of ANF layers and formed high-density electron traps, the breakdown strength of ANF/PMIA/ANF composite paper is significantly enhanced. The Weibull breakdown strength ANF/PMIA/ANF composite paper with 4 mg/mL of ANF are 82.7 MV/m at 25 °C and 61.7 MV/m at 100 °C, which are 165.1 and 137.4% of the A-P-A-0 at 25 and 100&#xa0;°C, respectively. Additionally, the flame-retardant property of ANF/PMIA/ANF composite paper is also obviously improved with increasing concentration of ANF. Consequently, this work offers an opportunity for the development of novel polymeric insulating paper with enhanced breakdown strength in a wide temperature range.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Novel Sandwich-Structured Flexible ANF/PMIA/ANF Composite Paper with Enhanced Breakdown Strength

  • 期刊论文

  • 发表日期：

    2025年2月27日

查看全文
  • Guangyu Duan,
  • Fengying Hu,
  • Yinghao Liang,
  • Duo Lu,
  • Wenxuan Shao,
  • Ruopu Xu,
  • Yabing Wang,
  • Zuming Hu

摘要

With the rapid development of cutting-edge electrical equipment and electrical systems, it is of great significance to develop advanced polymeric insulating paper with high breakdown strength under a high-temperature environment. In this paper, aramid nanofibers (ANF) and original poly(m-phenylene isophthalamide) (PMIA) paper were utilized to construct ANF/PMIA/ANF composite papers with sandwich structure. On account of the reduced surface roughness of the original PMIA paper, the high breakdown strength of ANF layers and formed high-density electron traps, the breakdown strength of ANF/PMIA/ANF composite paper is significantly enhanced. The Weibull breakdown strength ANF/PMIA/ANF composite paper with 4 mg/mL of ANF are 82.7 MV/m at 25 °C and 61.7 MV/m at 100 °C, which are 165.1 and 137.4% of the A-P-A-0 at 25 and 100 °C, respectively. Additionally, the flame-retardant property of ANF/PMIA/ANF composite paper is also obviously improved with increasing concentration of ANF. Consequently, this work offers an opportunity for the development of novel polymeric insulating paper with enhanced breakdown strength in a wide temperature range.