<p>In this study, EuCrO<sub>3</sub> (ECO) and Eu<sub>0.9</sub>Dy<sub>0.10</sub>CrO<sub>3</sub> (EDCO) rare-earth orthochromite compositions were synthesized through the traditional solid-state reaction technique. A comprehensive investigation was conducted to analyse the effect of the substitution of 10&#xa0;wt% Dy<sup>3+</sup> ions on the structural, optical and magnetic properties of EuCrO<sub>3</sub>. The X-ray diffraction results along with Rietveld refinement confirm the monophasic nature with an orthorhombic distorted perovskite structure for both compositions. Field emission scanning electron microscopy reveals polycrystalline microstructures with average grain sizes ranging from 269 to 327 nm for both compounds. The optical bandgap is evaluated by Tauc’s relation and is observed to slightly increase from 2.24 to 2.33 eV with Dy<sup>3+</sup> ions substitution. Optical parameters, including skin depth, extinction coefficient, refractive index and optical conductivity are determined and their variations with Dy substitution are analysed. Temperature-dependent magnetic analysis reveals a Néel temperature (<i>T</i><sub>N</sub>) of 177 K in EDCO composition, lower than that of pristine EuCrO<sub>3</sub> (<i>T</i><sub>N</sub> ~181 K). The magnetocaloric effect of the EDCO compound demonstrates a magnetic entropy change (Δ<i>S</i>) and relative cooling power of –0.27 J kg<sup>−1</sup> K and 4.4 J kg<sup>−1</sup>, respectively, near <i>T</i><sub>N</sub> under the application of 7 Tesla field. This study highlights the tunability of EuCrO<sub>3</sub> properties through Dy ion substitution for customized applications.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Tuning the structural, magnetic and optical properties of EuCrO3 orthochromites through Dy3+ substitution

  • 期刊论文

  • 发表日期：

    2025年1月11日

查看全文
  • Meenakshi,
  • R Kapoor,
  • S Dash,
  • R Bansal,
  • A Vij,
  • H K Chourasiya,
  • N Kumar,
  • Ramovatar,
  • S Kumar

摘要

In this study, EuCrO3 (ECO) and Eu0.9Dy0.10CrO3 (EDCO) rare-earth orthochromite compositions were synthesized through the traditional solid-state reaction technique. A comprehensive investigation was conducted to analyse the effect of the substitution of 10 wt% Dy3+ ions on the structural, optical and magnetic properties of EuCrO3. The X-ray diffraction results along with Rietveld refinement confirm the monophasic nature with an orthorhombic distorted perovskite structure for both compositions. Field emission scanning electron microscopy reveals polycrystalline microstructures with average grain sizes ranging from 269 to 327 nm for both compounds. The optical bandgap is evaluated by Tauc’s relation and is observed to slightly increase from 2.24 to 2.33 eV with Dy3+ ions substitution. Optical parameters, including skin depth, extinction coefficient, refractive index and optical conductivity are determined and their variations with Dy substitution are analysed. Temperature-dependent magnetic analysis reveals a Néel temperature (TN) of 177 K in EDCO composition, lower than that of pristine EuCrO3 (TN ~181 K). The magnetocaloric effect of the EDCO compound demonstrates a magnetic entropy change (ΔS) and relative cooling power of –0.27 J kg−1 K and 4.4 J kg−1, respectively, near TN under the application of 7 Tesla field. This study highlights the tunability of EuCrO3 properties through Dy ion substitution for customized applications.