<p>Ni-based alloys are strong candidates for use in high-temperature molten salt reactors due to their superior corrosion resistance and mechanical stability compared to stainless steels. In this study, the static corrosion behavior of a Ni-19Cr-5Fe model alloy was systematically evaluated in a purified molten NaCl-MgCl<sub>2</sub> salt at 700°C for 30, 240, and 500 h. Post-exposure analyses were conducted to assess microstructural evolution, corrosion depth, and elemental depletion profiles. Corrosion rates, quantified by chromium depletion depth, followed an inverse power-law trend with increasing exposure time, indicating diffusion-limited kinetics. This trend is attributed to limitations in mass transport in the static salt and to the progressive local depletion of reactive chromium species. Coupled electron backscatter diffraction and energy dispersive X-ray spectroscopy analysis further revealed that the grain boundary character significantly influences corrosion susceptibility: high-angle grain boundaries exhibited pronounced Cr depletion and pitting, while low-angle and Σ3 boundaries remained comparatively resistant. These results offer valuable insight into the role of microstructure in corrosion processes and reinforce the importance of time-dependent material evaluation in molten salt environments relevant to advanced reactor designs.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Corrosion Response of Ni-19Cr-5Fe in Molten NaCl-MgCl2 Salt

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年12月23日

查看全文
  • Robert Gentile,
  • Laura Hawkins,
  • Michael Woods,
  • Ruchi Gakhar,
  • Daniel Murray,
  • Lingfeng He

摘要

Ni-based alloys are strong candidates for use in high-temperature molten salt reactors due to their superior corrosion resistance and mechanical stability compared to stainless steels. In this study, the static corrosion behavior of a Ni-19Cr-5Fe model alloy was systematically evaluated in a purified molten NaCl-MgCl2 salt at 700°C for 30, 240, and 500 h. Post-exposure analyses were conducted to assess microstructural evolution, corrosion depth, and elemental depletion profiles. Corrosion rates, quantified by chromium depletion depth, followed an inverse power-law trend with increasing exposure time, indicating diffusion-limited kinetics. This trend is attributed to limitations in mass transport in the static salt and to the progressive local depletion of reactive chromium species. Coupled electron backscatter diffraction and energy dispersive X-ray spectroscopy analysis further revealed that the grain boundary character significantly influences corrosion susceptibility: high-angle grain boundaries exhibited pronounced Cr depletion and pitting, while low-angle and Σ3 boundaries remained comparatively resistant. These results offer valuable insight into the role of microstructure in corrosion processes and reinforce the importance of time-dependent material evaluation in molten salt environments relevant to advanced reactor designs.