<p>This study investigates the reduction mechanisms of pellets fabricated from phosphate ore powders under varying operational parameters (temperature, time, coal-to-ore ratio, and silica-to-lime molar ratio). Analytical techniques, including ash fusion temperature analysis, x-ray diffraction, and scanning electron microscopy, were employed. The results indicate that an optimal coal addition range of 20–24% and maintaining the silica-to-lime ratio of the concentrated ore powder at 1.0 yield superior pellet reduction performance. At lower reduction temperatures, silica reacts preferentially with fluorapatite to form Ca<sub>3</sub>(PO<sub>4</sub>)<sub>2</sub>. It subsequently reduces with carbon to form CaO, which reacts with SiO<sub>2</sub>, generating new silicate phases. As the temperature increases, the reduction rate of pellets rises, and solid particles transition into a molten state, facilitating the formation of a vitreous phase. The highest reduction rate of 93.72% was achieved at 1400&#xa0;°C using raw phosphate ore powder pellets. At 1450&#xa0;°C, reduction rates for pellets made from concentrated phosphate ore and mixed ore types reached 89.1% and 91.33%, respectively. It was demonstrated that pellets formulated from a blend of high-grade concentrated ore powder and low-grade raw ore powder could substantially lower the reduction temperature and reduce energy consumption, all while maintaining a high reduction rate.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Influence and Mechanism on the Preparation of Pellets Using Phosphate Ore Powder

  • 期刊论文

  • 发表日期：

    2025年7月2日

查看全文
  • Dongsheng He,
  • Yuanhao Zhang,
  • Yanhong Fu,
  • Yangyang Cao,
  • Yuan Tang,
  • Zhili Li,
  • Qiu Yang

摘要

This study investigates the reduction mechanisms of pellets fabricated from phosphate ore powders under varying operational parameters (temperature, time, coal-to-ore ratio, and silica-to-lime molar ratio). Analytical techniques, including ash fusion temperature analysis, x-ray diffraction, and scanning electron microscopy, were employed. The results indicate that an optimal coal addition range of 20–24% and maintaining the silica-to-lime ratio of the concentrated ore powder at 1.0 yield superior pellet reduction performance. At lower reduction temperatures, silica reacts preferentially with fluorapatite to form Ca3(PO4)2. It subsequently reduces with carbon to form CaO, which reacts with SiO2, generating new silicate phases. As the temperature increases, the reduction rate of pellets rises, and solid particles transition into a molten state, facilitating the formation of a vitreous phase. The highest reduction rate of 93.72% was achieved at 1400 °C using raw phosphate ore powder pellets. At 1450 °C, reduction rates for pellets made from concentrated phosphate ore and mixed ore types reached 89.1% and 91.33%, respectively. It was demonstrated that pellets formulated from a blend of high-grade concentrated ore powder and low-grade raw ore powder could substantially lower the reduction temperature and reduce energy consumption, all while maintaining a high reduction rate.