Enhancement of Cobalt Bismuth Nano-Ferrite via Heat Treatment to be Applied in High-Frequency and Antimicrobial Applications

Cobalt bismuth nano-ferrite (Co/Bi) with the chemical formula CoBi_0.02Fe_1.98O₄ was produced using a simple flash auto-combustion method at three different temperatures: as-prepared, 600°C, and 800°C. A single-phase spinel structure was confirmed using X-ray diffraction, and the nano-scale morphology was examined using AFM (atomic force microscopy). Magnetic measurements demonstrated that increasing the annealing temperature increased the saturation magnetization M_s by 1.3 times. However, the coercivity H_c changed from semi-hard ferrite (as-prepared sample) to soft ferrite (Co/Bi nano-ferrite at 800°C) and reduced 10.7 times that of as-prepared nanoparticles. Therefore, the 800°C Co/Bi nano-ferrite with a low coercive field is recommended for transformers, recording heads, inductor cores, magnetic shielding, and microwave devices. The as-prepared sample and that at 600°C displayed super-high microwave frequency (SHF) in the X band in high-frequency applications calculated from magnetic measurement. The 800°C sample also has an extremely high microwave frequency in the Ku band, which is utilized in radar and satellite communications. Antimicrobial characterization showed that raising the annealing temperature increased the effectiveness of the samples against tested microorganisms. Thus, the samples under investigation are highly suggested for ultra-high microwave frequency applications and biological antibacterial nanomaterials.