<p>Aseptic loosening and abrasion of implants are significant challenges in knee arthroplasty. In particular, the wear of ultra-high molecular weight polyethylene (UHMWPE) inlays can lead to prosthesis failure. The early detection of wear is complicated by the low radiopacity of the material. A promising method for detecting wear is the integration of radiopaque markers into the implant surface. This work focuses on the micro-structuring of UHMWPE to incorporate such markers using micro-milling processes. Experimental milling experiments were carried out with different tool diameters, whereby various milling strategies, cutting parameters, and approach strategies were analyzed. A central challenge was the formation of burrs, which makes subsequent marker insertion difficult. The influence of the process parameters on burr formation was investigated by systematically varying the process control variables. The results indicate that the identified process windows (d<sub>T</sub> = 0.6&#xa0;mm, z = 2, a<sub>e</sub> = 0.05&#xa0;mm, a<sub>p</sub> = 0.15–0.2&#xa0;mm, f<sub>z</sub> = 0.0123–0.02&#xa0;mm, and v<sub>c</sub> = 25–30&#xa0;m/min) resulted, on average, in a significant reduction of burr formation by 69%. In addition, the transferability of the determined process control variables to free-form surfaces was investigated. For this purpose, kinematic process parameters were determined by dexel-based material removal simulation. The results show a low reproducibility of burr formation due to inconstant cutting conditions (depth of cut and width of cut).</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Analysis on micro-milling of UHMWPE for the integration of radiopaque markers on the surface of TKA inlays

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2025年12月4日

查看全文
  • Berend Denkena,
  • Klaas Maximilian Heide,
  • Max-Enno Eggers,
  • Crystal Kayaro Emonde,
  • Christof Hurschler

摘要

Aseptic loosening and abrasion of implants are significant challenges in knee arthroplasty. In particular, the wear of ultra-high molecular weight polyethylene (UHMWPE) inlays can lead to prosthesis failure. The early detection of wear is complicated by the low radiopacity of the material. A promising method for detecting wear is the integration of radiopaque markers into the implant surface. This work focuses on the micro-structuring of UHMWPE to incorporate such markers using micro-milling processes. Experimental milling experiments were carried out with different tool diameters, whereby various milling strategies, cutting parameters, and approach strategies were analyzed. A central challenge was the formation of burrs, which makes subsequent marker insertion difficult. The influence of the process parameters on burr formation was investigated by systematically varying the process control variables. The results indicate that the identified process windows (dT = 0.6 mm, z = 2, ae = 0.05 mm, ap = 0.15–0.2 mm, fz = 0.0123–0.02 mm, and vc = 25–30 m/min) resulted, on average, in a significant reduction of burr formation by 69%. In addition, the transferability of the determined process control variables to free-form surfaces was investigated. For this purpose, kinematic process parameters were determined by dexel-based material removal simulation. The results show a low reproducibility of burr formation due to inconstant cutting conditions (depth of cut and width of cut).