<p>The longitudinal and transverse cracks were discovered at the center position of the 40Cr drive shaft quenched and tempered during machining in an enterprise. The cracking causes of the drive shaft were analyzed through chemical composition analysis, macroscopic and microscopic morphology observation of fracture surfaces, energy dispersive X-ray spectroscopy analysis, analysis of non-metallic inclusions, and microstructure analysis. The results indicate that the cracking reason of the shaft is caused by the combined action of the increased quenching stress caused by the banded structure and the presence of sulfide inclusions. The existence of banded structures leads to a significant increase in stress during quenching, causing cracks to form at sulfide inclusions, which then propagate into internal cracks distributed longitudinally. The fracture mechanism is brittle fracture.</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Cracking Failure Analysis of 40Cr Drive Shaft

  • 期刊论文

  • 发表日期：

    2025年2月2日

查看全文
  • Lan Wang,
  • Ruo-Fei Du,
  • Xu-Feng Zhang,
  • Cheng-Yu Jia,
  • An-Tao Cai

摘要

The longitudinal and transverse cracks were discovered at the center position of the 40Cr drive shaft quenched and tempered during machining in an enterprise. The cracking causes of the drive shaft were analyzed through chemical composition analysis, macroscopic and microscopic morphology observation of fracture surfaces, energy dispersive X-ray spectroscopy analysis, analysis of non-metallic inclusions, and microstructure analysis. The results indicate that the cracking reason of the shaft is caused by the combined action of the increased quenching stress caused by the banded structure and the presence of sulfide inclusions. The existence of banded structures leads to a significant increase in stress during quenching, causing cracks to form at sulfide inclusions, which then propagate into internal cracks distributed longitudinally. The fracture mechanism is brittle fracture.