Metallurgical Analysis of Lower Mechanical Property in 17-4PH Steel: A Comprehensive Study
摘要
This paper presents a comprehensive metallurgical analysis conducted on representative samples obtained from two batches of 17-4PH steel rods in order to investigate the underlying factors contributing to the observed differences in their mechanical properties. The samples underwent a solution annealing process followed by an aging treatment to achieve H1025 temper condition. Surprisingly, the mechanical properties of one batch namely 91/5 were found to be inferior compared to the other batch 91/7, with only the latter meeting the specified requirements. To gain a deeper understanding of these differences, a range of analytical techniques were employed. Local variation in austenite stabilizers and its corresponding effect on microstructure of batch 91/5 was found to be the root cause of lower mechanical property.