<p>The passivation behavior of cold-sprayed 316L stainless steel coatings deposited onto SAE 1020 carbon steel was investigated with particular emphasis on the influence of surface condition and deposition temperature. Coatings produced at gas temperatures of 650-825&#xa0;°C exhibited thicknesses of ~ 450-520&#xa0;<i>µ</i>m and porosity levels of ~ 5-7&#xa0;vol.%, with microstructures characterized by interparticle boundaries and incomplete bonding typical of cold-sprayed deposits. Electrochemical performance was evaluated in 0.6&#xa0;M NaCl solution using open circuit potential (OCP), electrochemical impedance spectroscopy (EIS), and cyclic potentiodynamic polarization (CPP). In the polished condition, the coatings consistently exhibited a shift toward more noble OCP values compared to both the as-sprayed state and the SAE 1020 substrate, indicating enhanced surface stability. Despite moderate polarization resistance and the presence of microstructural heterogeneities, EIS results revealed capacitive responses associated with passive-like surface films. Cyclic polarization further demonstrated that polished coatings are capable of sustaining anodic polarization without abrupt current increase, in contrast to the active behavior of the substrate, and in some cases showed evidence of repassivation. These findings indicate that surface finishing plays a critical role in stabilizing passive-like behavior, even in the presence of residual porosity. Overall, the results demonstrate that polished cold-sprayed 316L coatings effectively promote passivation and significantly improve the corrosion resistance of carbon steel substrates in chloride-containing environments. </p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Corrosion Behavior of Cold-Sprayed 316L Coatings: Effects of Deposition Temperature and Surface Condition

  • 期刊论文

  • 出版模式：

    开放获取

  • 发表日期：

    2026年7月29日

查看全文
  • Brenda Juliet Martins Freitas,
  • Vinicius Gustavo da Cruz,
  • Alexandre Romão Costa Nascimento,
  • Luc Pouliot,
  • Bruna Fernanda Batistão,
  • Eduardo Campos Payao da Silva,
  • Piter Gargarella,
  • Claudemiro Bolfarini,
  • Guilherme Yuuki Koga

摘要

The passivation behavior of cold-sprayed 316L stainless steel coatings deposited onto SAE 1020 carbon steel was investigated with particular emphasis on the influence of surface condition and deposition temperature. Coatings produced at gas temperatures of 650-825 °C exhibited thicknesses of ~ 450-520 µm and porosity levels of ~ 5-7 vol.%, with microstructures characterized by interparticle boundaries and incomplete bonding typical of cold-sprayed deposits. Electrochemical performance was evaluated in 0.6 M NaCl solution using open circuit potential (OCP), electrochemical impedance spectroscopy (EIS), and cyclic potentiodynamic polarization (CPP). In the polished condition, the coatings consistently exhibited a shift toward more noble OCP values compared to both the as-sprayed state and the SAE 1020 substrate, indicating enhanced surface stability. Despite moderate polarization resistance and the presence of microstructural heterogeneities, EIS results revealed capacitive responses associated with passive-like surface films. Cyclic polarization further demonstrated that polished coatings are capable of sustaining anodic polarization without abrupt current increase, in contrast to the active behavior of the substrate, and in some cases showed evidence of repassivation. These findings indicate that surface finishing plays a critical role in stabilizing passive-like behavior, even in the presence of residual porosity. Overall, the results demonstrate that polished cold-sprayed 316L coatings effectively promote passivation and significantly improve the corrosion resistance of carbon steel substrates in chloride-containing environments.