Devitrification-Induced Tailoring of Microstructure and Strength in Aluminum High-Entropy Alloy Powder for Cold Spray Deposition

The development of high-strength cold spray deposits using amorphous/nanocrystalline aluminum high-entropy alloy (Al HEA) powder is hindered by the lack of understanding of correlations between powder microstructure and its deformation behavior. In this study, gas-atomized Al HEA powder (Al_90.05-Y_4.4-Ni_4.3-Co_0.9-Sc_0.35 at.%) is devitrified at 298, 345, 362, and 450 °C to optimize strength and deformation for cold spraying. Devitrification-induced atomic rearrangement developed equiaxed Al grains and Al₃Ni and Al₃Sc precipitates. The amorphous content, growth of grains, hard precipitates, and reduced dislocation density increased the hardness by 16% to 515 HV at 298 °C and decreased the hardness by 55% to 190 HV at 450 °C. The compressive strength of Al HEA powder increased by 5% to 1559 MPa at 298 °C and decreased by 49% to 760 MPa at 450 °C. To enhance the limited sprayability of Al HEA powder, compressive strength is used to model optimized cold spray process maps. Helium gas with temperatures from 300 to 800 °C and a pressure of 40 bar can produce cold spray deposits with deposition efficiency greater than 70%. The scientific insights acquired from the present study provide a gateway toward developing novel lightweight and high-strength aluminum alloy deposits, thus marking an advancement in cold spray technology.