<p>The impact of microstructure on the corrosion behavior of V-N-Cr microalloyed added weathering steels was investigated using various materials characterization techniques including optical microscopy (OM), scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD), electron probe microanalysis (EPMA), potentiodynamic polarization tests, and electrochemical impedance spectroscopy (EIS). These methods were employed to analyze the corroded layer, identify principal phases, and observe morphology. The microstructure of V-N-Cr microalloyed added weathering steel, which includes ferrite, granular bainite, acicular ferrite, and a small amount of fine pearlite after cooling at 590&#xa0;°C. Polygonal ferrite, lamellar bainite, granular bainite, and some acicular ferrite were present after cooling at 420&#xa0;°C. Results from wet/dry cyclic corrosion tests showed that Type 2&#xa0;V-N-Cr microalloyed added weathering steel (cooled at 590&#xa0;°C) exhibited greater corrosion resistance compared to Type 1 steel (cooled at 420&#xa0;°C), forming a protective barrier layer that effectively stabilizes the corrosion rate. The fine precipitates contributed to the development of a thicker, denser, and more stable corroded layer in the steel under investigation. Exposure of V-N-Cr microalloyed added weathering steels to a simulated industrial atmosphere resulted in the formation of various corrosion products, predominantly iron-rich oxides such as γ-FeOOH (lepidocrocite), α-FeOOH (goethite), Fe<sub>3</sub>O<sub>4</sub> and Fe<sub>2</sub>O<sub>3</sub> (hematite).</p>

错误：搜索内容不能为空，请输入英文关键词
错误：关键词超出字数限制，请精简
高级检索

Influence of Microstructure on the Corrosion Behavior of V-N-Cr Microalloyed Added Weathering Steels

  • 期刊论文

  • 发表日期：

    2025年3月21日

查看全文
  • Yue Liu,
  • Xiao-Ming Zheng,
  • Qiu-Ming Li,
  • Lin-Xiu Du,
  • Zhi-Nan Yang

摘要

The impact of microstructure on the corrosion behavior of V-N-Cr microalloyed added weathering steels was investigated using various materials characterization techniques including optical microscopy (OM), scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD), electron probe microanalysis (EPMA), potentiodynamic polarization tests, and electrochemical impedance spectroscopy (EIS). These methods were employed to analyze the corroded layer, identify principal phases, and observe morphology. The microstructure of V-N-Cr microalloyed added weathering steel, which includes ferrite, granular bainite, acicular ferrite, and a small amount of fine pearlite after cooling at 590 °C. Polygonal ferrite, lamellar bainite, granular bainite, and some acicular ferrite were present after cooling at 420 °C. Results from wet/dry cyclic corrosion tests showed that Type 2 V-N-Cr microalloyed added weathering steel (cooled at 590 °C) exhibited greater corrosion resistance compared to Type 1 steel (cooled at 420 °C), forming a protective barrier layer that effectively stabilizes the corrosion rate. The fine precipitates contributed to the development of a thicker, denser, and more stable corroded layer in the steel under investigation. Exposure of V-N-Cr microalloyed added weathering steels to a simulated industrial atmosphere resulted in the formation of various corrosion products, predominantly iron-rich oxides such as γ-FeOOH (lepidocrocite), α-FeOOH (goethite), Fe3O4 and Fe2O3 (hematite).